PolyOne Nymax™ GF 1200 A 33 HS Black 22 Polyamide 66 (Nylon 66)

Category	Polymer , Thermoplastic , Nylon , Nylon 66
Manufacturer	PolyOne Corporation
Trade Name	Nymax™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Nymax™ GF 1200 A 33 HS Black 22 Polyamide 66 (Nylon 66).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

The Nymax® GF 1200 Series of glass fiber-reinforced nylon 6/6 compounds have been specifically formulated for applications requiring high stiffness, tensile properties, heat resistance, and durability in harsh environments. These materials are available in a broad range of reinforcement levels depending upon stiffness characteristics desired and have been formulated to offer ease of processing in most standard thermoplastic processing equipmentMolded Test Bars: Dry as MoldedInformation provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.38 g/cc	1.38 g/cc	ASTM D792
Water Absorption	1.0 % @Thickness 3.18 mm	1.0 % @Thickness 0.125 in	@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.0020 - 0.0040 cm/cm	0.0020 - 0.0040 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	193 MPa	28000 psi	Type I, 5.1 mm/min; ASTM D638
Tensile Strength, Yield	184 MPa	26700 psi	5.0 mm/min; ISO 527
Elongation at Break	3.0 - 4.0 %	3.0 - 4.0 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	8.62 GPa	1250 ksi	ASTM D638
Flexural Strength	248 MPa	36000 psi	ASTM D790
Flexural Modulus	8.62 GPa	1250 ksi	ASTM D790
	9.35 GPa	1360 ksi	ISO 178
Izod Impact, Notched	1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Izod Impact, Notched (ISO)	13.0 kJ/m²	6.19 ft-lb/in²	ISO 180

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	245 °C	473 °F	Unannealed; ISO 75-2
	245 °C @Thickness 3.18 mm	473 °F @Thickness 0.125 in	Unannealed; ASTM D648

Processing Properties	Metric	English
Mold Temperature	60.0 - 107 °C	140 - 225 °F
Drying Temperature	82.2 °C	180 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Additive	Heat Stabilizer
Appearance	Black
Automotive Specifications	FORD ESE-M4D287-A
	FORD ESE-M4D287-B
Features	General Purpose
	Heat Stabilized
Filler / Reinforcement	Glass Fiber Reinforcement, 33% Filler by Weight
Forms	Pellets
Generic Material	Nylon 66
Generic Name	Polyamide 66 (Nylon 66)
Processing Method	Injection Molding
Regional Availability	North America
	South America
Uses	Automotive Applications
	Construction Applications
	Consumer Applications
	General Purpose
	Industrial Applications