Materion Beryllium Copper Alloy 10C Castings (UNS C82000)

Category	Metal , Nonferrous Metal , Beryllium Alloy , Copper Alloy
Manufacturer	Materion Corporation (former Brush Wellman)
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Materion Beryllium Copper Alloy 10C Castings (UNS C82000).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Pouring Temperature: 1095-1175Â°CHeat treatment required for max strength (Annealing): 870-900Â°C/water quenchHeat treatment required for max strength (Hardening): 870-900Â°C/water quenchTabulated properties apply to products after age hardening. Information supplied by Brush Wellman.Brush Engineered Materials Inc. changed its name to Materion Corporation in March 2011.

Physical Properties	Metric	English	Comments
Density	8.83 g/cc	0.319 lb/inÂ³

Mechanical Properties	Metric	English	Comments
Hardness, Rockwell B	92 - 100	92 - 100
Tensile Strength, Ultimate	620 - 750 MPa	89900 - 109000 psi	Solution Annealed and Aged
Tensile Strength, Yield	480 - 560 MPa	69600 - 81200 psi	Solution Annealed and Aged
Elongation at Break	3.0 - 15 %	3.0 - 15 %	Solution Annealed & Aged
Modulus of Elasticity	138 GPa	20000 ksi

Thermal Properties	Metric	English
CTE, linear	18.0 Âµm/m-Â°C @Temperature 20.0 - 200 Â°C	10.0 Âµin/in-Â°F @Temperature 68.0 - 392 Â°F
Thermal Conductivity	195 W/m-K	1350 BTU-in/hr-ftÂ²-Â°F
Melting Point	1000 - 1030 Â°C	1830 - 1890 Â°F
Solidus	1000 Â°C	1830 Â°F
Liquidus	1030 Â°C	1890 Â°F

Component Elements Properties	Metric	English	Comments
Beryllium, Be	0.45 - 0.80 %	0.45 - 0.80 %
Cobalt, Co	2.4 - 2.7 %	2.4 - 2.7 %
Copper, Cu	97 %	97 %	as balance

Electrical Properties	Metric	English	Comments
Electrical Resistivity	0.00000340 - 0.00000380 ohm-cm	0.00000340 - 0.00000380 ohm-cm	45-50% IACS Conductivity