- Multibase Nylex™ 2185 CR Polyamide + PP
Multibase Nylex™ 2185 CR Polyamide + PP
| Category | Polymer , Thermoplastic , Nylon , Polypropylene (PP) |
| Manufacturer | Multibase |
| Trade Name | Nylex™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Multibase Nylex™ 2185 CR Polyamide + PP.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Forms: PelletsFeatures:Chemical Resistance, GoodInformation provided by Multibase
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM 792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM D955 |
| Melt Flow | 1.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
1.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 42.1 MPa | 6100 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Flexural Strength | 49.6 MPa | 7200 psi | ASTM D790 |
| Flexural Modulus | 1.48 GPa | 215 ksi | Method I (3 point load), Procedure B); ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm | 1.10 ft-lb/in | ASTM D256 |
| Gardner Impact | 2.260 J | 1.667 ft-lb | ASTM D3029 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 66.1 °C | 151 °F | Unannealed; ASTM D648 |
| Flammability, UL94 | HB | HB |
Users viewing this material also viewed the following:
- IDI Composites M-207 Thermoset Polyester, Sheet
- LATI Latamid 66 H2 G/50 PA 66, 50% Glass Fiber Reinforced, Heat Stabilized
- A. Schulman POLYFORT™ FPP 1285 Glass Fiber-Reinforced Copolymer Polypropylene
- Unitika TERRAMAC TP-4030 Polylactic Acid (PLA)
- Dow Corning DM1 Demulsifier
- Dow Corning 2-3899 Antifoam Compound
- Chicago Extruded Metals BioBrass® UNS C22000 Copper-Zinc Alloy
- Arlon LW50125Rxx-P0 0.050" (1.27 mm) Cured Self-Fusing Silicone Tape (Triangular, Unsupported)
- Cheng Yu Plastic IPS610BK Electric Conducting HIPS, Extrusion
- Resinlab® TL5072 Anaerobic Threadlocking Compound
Copyright © lookpolymers.com All Rights Reserved