PolyOne Nymax™ GB 1200 20 HS BLACK 18 Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Nymax™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Nymax™ GB 1200 20 HS BLACK 18 Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Preliminary Data SheetMolded Test Bars: Dry as MoldedInformation provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.28 g/cc | 1.28 g/cc | ASTM D792 |
| Water Absorption | 0.90 % @Thickness 3.18 mm |
0.90 % @Thickness 0.125 in |
@ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | ASTM D955 |
| Ash | 20 % | 20 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 62.1 MPa | 9010 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 3.79 GPa | 550 ksi | ASTM D790 |
| Izod Impact, Notched | 0.320 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
0.599 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 265 °C | 509 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C @Thickness 3.18 mm |
428 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C @Thickness 3.18 mm |
185 °F @Thickness 0.125 in |
Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Mold Temperature | 60.0 - 107 °C | 140 - 225 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 4.00 hour | 4.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Heat Stabilizer | |
| Appearance | Black | |
| Features | Heat Stabilized | |
| Filler / Reinforcement | Glass Bead | |
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Regional Availability | North America | |
| South America |
Users viewing this material also viewed the following:
- Pyrotek Pyrocast AR70 Low-Density Refractory Castable
- Precision Polymer Engineering E50E Ethylene Propylene Rubber
- M. Holland Company GS230WC Polystyrene, Specialty
- Kolon KOPA® KN3322V0Y Flame Retardant Nylon 66
- Hexcel® HexPly® F155 Epoxy Resin, T3T095 Carbon Tape
- Arkema Group Pebax® MX 1059 Polyether Block Amide (PEBA) (Dry)
- Arlon 32400R060 0.060" (1.52 mm) Uncured Silicone Rubber on PET Carrier
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 60 PHR N330 Filler
- Permabond 792 Cyanoacrylate, Surface insensitive
- STAR Thermoplastic Alloys & Rubbers StarFlex® P 7380-9000 TPE
Copyright © lookpolymers.com All Rights Reserved