PolyOne LubriOne™ AT-000/15T Acetal (POM) Copolymer

Category	Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced
Manufacturer	PolyOne Corporation
Trade Name	LubriOne™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne LubriOne™ AT-000/15T Acetal (POM) Copolymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

LubriOne™ Lubricated and Wear-Resistant Compounds have been specifically formulated to be self-lubricating materials, offering low coefficient of friction and improved wear resistance properties. LubriOne compounds have been demonstrated to reduce friction, noise, vibration, heat buildup and improve product durability.Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	1.48 g/cc	1.48 g/cc	ASTM D792
Water Absorption	0.15 % @Thickness 3.18 mm	0.15 % @Thickness 0.125 in	@ 24 hrs; ASTM D570
Linear Mold Shrinkage, Flow	0.020 - 0.023 cm/cm	0.020 - 0.023 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	44.8 MPa	6500 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	7.0 - 8.0 %	7.0 - 8.0 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	2.24 GPa	325 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	72.4 MPa	10500 psi	ASTM D790
Flexural Modulus	2.24 GPa	325 ksi	ASTM D790
Izod Impact, Notched	0.480 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	0.899 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Coefficient of Friction, Dynamic	0.36	0.36	vs. Steel - Dynamic; ASTM D1894
Coefficient of Friction, Static	0.18	0.18	vs. Steel - Static; ASTM D1894

Thermal Properties	Metric	English	Comments
Deflection Temperature at 0.46 MPa (66 psi)	160 °C @Thickness 6.35 mm	320 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	154 °C @Thickness 6.35 mm	309 °F @Thickness 0.250 in	Unannealed; ASTM D648
Flammability, UL94	HB	HB	UL 94

Processing Properties	Metric	English	Comments
Melt Temperature	188 - 210 °C	370 - 410 °F

Descriptive Properties	Value	Comments
Features	Copolymer
	Good Wear Resistance
	Low Friction
	Lubricated
Forms	Pellets
Generic Material	Acetal (POM) Copolymer
Generic Name	Acetal (POM) Copolymer
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	South America
RoHS Compliance	RoHS Compliant
Uses	Appliance Components
	Automotive Applications
	Bearings
	Business Equipment
	Consumer Applications
	Conveyor Parts
	Gears
	Industrial Applications
	Printer Parts
	Pulleys
	Rollers