PolyOne Lubri-Tech™ AT-20GB/15T Acetal-Copolymer, Glass Bead Filled, PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AT-20GB/15T Acetal-Copolymer, Glass Bead Filled, PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description/Features:Glass Bead FilledPTFE LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.642 g/cc | 1.642 g/cc | ASTM D792 |
| Water Absorption | 0.10 % | 0.10 % | 24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.0080 - 0.0090 cm/cm | 0.0080 - 0.0090 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 37.9 MPa | 5500 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Elongation at Break | 4.0 % | 4.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.41 GPa | 350 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 37.9 MPa | 5500 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.587 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
1.10 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 193 - 216 °C | 380 - 420 °F | Molding |
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 2 hour | 2 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Product Form | Pellets |
Users viewing this material also viewed the following:
- Multibase Multi-Pro® 4003 RC 40% Glass Filled Polypropylene
- Kazanorgsintez PE2NT 17-11 Linear Low Density Polyethylene
- Silon Tabond 5010 Adhesive Resin
- Wolf Kunststoff ZEDEX® ZX-324VMT A3B PEEK, Fiber Reinforced
- Polyram RamTal PM8515 Acetal, High impact
- Clariant Renol PPSP0004 Polypropylene, Random Copolymer
- Eurotec® Tecomid® NB40 KK30 NL PA 6 30% glass fiber/mineral reinforced, low warpage
- BASF Ultramid® C3U10 BK 23079 PA6/66 FR (Dry)
- Adell EA-18 Homopolymer Polypropylene, 40% Talc Filled
- Solvay Specialty Polymers Ixef® 2530/X9027 Polyarylamide, 55% Mineral + Glass Fiber, at Equilibrium (65% RH)
Copyright © lookpolymers.com All Rights Reserved