- PolyOne Lubri-Tech™ AT-000/20T Copolymer Acetal - 20% PTFE Lubricated (discontinued **)
PolyOne Lubri-Tech™ AT-000/20T Copolymer Acetal - 20% PTFE Lubricated (discontinued **)
| Category | Polymer , Thermoplastic , Acetal (POM) |
| Manufacturer | |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Lubri-Tech™ AT-000/20T Copolymer Acetal - 20% PTFE Lubricated
(discontinued **).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by PolyOne.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.51 g/cc | 1.51 g/cc | ASTM D792 |
| Water Absorption | 0.18 % @Thickness 3.17 mm |
0.18 % @Thickness 0.125 in |
24 hr. Immersion; ASTM D570 |
| Linear Mold Shrinkage | 0.020 - 0.023 cm/cm | 0.020 - 0.023 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 44.8 MPa | 6500 psi | Type 1 - Rigids, Yield, 0.2 in/min; ASTM D638 |
| Elongation at Break | 7.0 - 9.0 % | 7.0 - 9.0 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Tensile Modulus | 2.24 GPa | 325 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 |
| Flexural Strength | 72.4 MPa | 10500 psi | ASTM D790 |
| Flexural Modulus | 2.24 GPa | 325 ksi | ASTM D790 |
| Izod Impact, Notched | 0.481 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
0.900 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Method A, Injection Molded; ASTM D256 |
| Coefficient of Friction | 0.30 | 0.30 | vs Steel; ASTM D1894 |
| Coefficient of Friction, Static | 0.18 | 0.18 | vs Steel; ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 °C | 310 °F | Unannealed; ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 188 - 210 °C | 370 - 410 °F | Molding |
Users viewing this material also viewed the following:
- Resinlab® EP1287 Filled, Flame Retardant Epoxy Syntactic Foam
- Potters Industries A-Series P-0337 Soda-Lime Silica Technical Quality Solid Glass Spheres
- Polymer Resources AH-GP2 Acetal Homopolymer, Medium Flow, Heat Stabilized
- PTS Trilac® ABS-HS5500 High Impact ABS Resin
- Karina E 1-/105-FC-LMPA White Color Concentrate for PVC
- Haynes Hastelloy® C-22HS™ Nickel Alloy Synergic Gas Metal Arc Welded (GMAW) All Weld Cruciform
- Trimay® Wear Plate TWP170 Flux Cored Weld Wire & Electrode
- DuPont Teijin Films Melinex® ST339 Polyester Film, 200 Gauge
- Arlon 0.027" (0.6858 mm) Flexible Heater Silicone with Fiberglass Substrate (56586R028)
- 3M FV034 Indoor UL Recognized White Vinyl Label Products
Copyright © lookpolymers.com All Rights Reserved