PolyOne Gravi-Tech™ GRV-NP-110-W-NAT Polyamide 12 (Nylon 12)

Category	Polymer , Thermoplastic , Nylon , Nylon 12
Manufacturer	PolyOne Corporation
Trade Name	Gravi-Tech™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	PolyOne Gravi-Tech™ GRV-NP-110-W-NAT Polyamide 12 (Nylon 12).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Information provided by PolyOne

Physical Properties	Metric	English	Comments
Specific Gravity	11.0 g/cc	11.0 g/cc	ASTM D792
Linear Mold Shrinkage, Flow	0.0040 - 0.0060 cm/cm	0.0040 - 0.0060 in/in	ASTM D955

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	27.2 MPa	3950 psi	Type I, 5.1 mm/min; ASTM D638
Elongation at Break	1.8 %	1.8 %	Type I, 5.1 mm/min; ASTM D638
Tensile Modulus	8.27 GPa	1200 ksi	Type I, 5.1 mm/min; ASTM D638
Flexural Strength	48.3 MPa	7010 psi	ASTM D790
Flexural Modulus	4.96 GPa	719 ksi	ASTM D790
Poissons Ratio	0.35	0.35	ASTM E132
Shear Modulus	3.06 GPa	444 ksi	Calculated
Izod Impact, Notched	1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256A
Izod Impact, Unnotched	3.70 J/cm @Thickness 3.18 mm, Temperature 23.0 °C	6.93 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F	Injection Molded; ASTM D256

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	63.0 µm/m-°C @Temperature 0.000 - 32.0 °C	35.0 µin/in-°F @Temperature 32.0 - 89.6 °F	ASTM E831
	100 µm/m-°C @Temperature 60.0 - 100 °C	55.6 µin/in-°F @Temperature 140 - 212 °F	ASTM E831
CTE, linear, Transverse to Flow	57.0 µm/m-°C @Temperature 0.000 - 32.0 °C	31.7 µin/in-°F @Temperature 32.0 - 89.6 °F	ASTM E831
	84.0 µm/m-°C @Temperature 60.0 - 100 °C	46.7 µin/in-°F @Temperature 140 - 212 °F	ASTM E831
Thermal Conductivity	3.50 W/m-K	24.3 BTU-in/hr-ft²-°F	The value listed as thermal conductivity, ASTM C177, was tested in accordance with ASTM E1461.; ASTM C177
Deflection Temperature at 0.46 MPa (66 psi)	138 °C @Thickness 6.35 mm	280 °F @Thickness 0.250 in	Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi)	87.8 °C @Thickness 6.35 mm	190 °F @Thickness 0.250 in	Unannealed; ASTM D648

Processing Properties	Metric	English
Melt Temperature	260 - 288 °C	500 - 550 °F
Mold Temperature	82.2 - 149 °C	180 - 300 °F
Drying Temperature	79.4 °C	175 °F
Dry Time	4.00 hour	4.00 hour

Descriptive Properties	Value	Comments
Additive	Impact Modifier
Appearance	Natural Color
Features	High Density
	Impact Modified
	Non-Toxic
Forms	Pellets
Generic Material	Nylon 12
Generic Name	Polyamide 12 (Nylon 12)
Processing Method	Injection Molding
Regional Availability	Africa & Middle East
	Asia Pacific
	Europe
	North America
	South America
Uses	Industrial Applications
	Medical/Healthcare Applications
	Projectiles
	Radiation Shielding
	Sporting Goods
	Weighting & Balancing