Dow Buna® cis 132 High-cis polybutadiene rubber (nickel catalyzed) for tires and rubber articles

Category Polymer
Manufacturer Dow Chemical
Trade Name Buna®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow Buna® cis 132 High-cis polybutadiene rubber (nickel catalyzed) for tires and rubber articles.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Buna® cis 132 - Schkopau is a stereospecific polybutadiene with high cis-1,4 content. It is manufactured by a solution process using an organo-metallic catalyst which produces a consistent light colored polymer with low ash content. It contains a non-staining stabilizer. Buna® cis 132 is widely used in the tire industry but also in the manufacture of conveyor belts and other rubber articles which are exposed to high stress. It offers good abrasion resistance, high resilience, low hysteresis, and low glass transition point which results in better low temperature performance. Buna® cis 132 offers excellent processability and may be blended with natural rubber and styrene butadiene (SBR), isoprene (IR), nitrile (NBR), or polychloroprene (CR) synthetic rubbers. The non-staining stabilizer allows manufacture of colored rubber articles also when compounded with selected thermoplastics. It is supplied in bales weighing 25 kg. Bales are wrapped in 50 micron PE film.Information provided by Dow
Physical Properties Metric English Comments
Viscosity Measurement 3.1
3.1
[min]; ts1; ASTM D5289
6.9
6.9
[min]; t<sub>c</sub>(50); ASTM D5289
10.5
10.5
[min]; t<sub>c</sub>(90); ASTM D5289
16
16
[dNm]; MH; ASTM D5289
2.6

@Temperature 160 °C
2.6

@Temperature 320 °F
[dNm]; ML; ASTM D5289
Mooney Viscosity 45

@Temperature 100 °C
45

@Temperature 212 °F
[MU]; ML 1+4; ASTM D1646
Ash 0.050 %
0.050 %
ASTM D5667
Collected Volatile Condensable Material 0.25 %
0.25 %
ASTM D5668
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 17.5 MPa
2540 psi
Cure: 35 min at 145°C; ASTM D412
Tensile Strength, Yield 9.00 MPa

@Strain 300 %
1310 psi

@Strain 300 %
ASTM D412
Elongation at Break 510 %
510 %
ASTM D412
Processing Properties Metric English Comments
Shelf Life >= 12.0 Month
>= 12.0 Month
Descriptive Properties Value Comments
Accelerator (TBBS) wt% 0.9
ASTM D3189
Carbon Black wt% 60
ASTM D3189; IRB 7
Cis-1,4 Content % 95
Supplier Method (FTIR)
Stearic Acid wt% 2
ASTM D3189
Sulfur content, % 1.5
ASTM D3189
Zinc Oxide wt% 3
ASTM D3189