PolyOne Geon™ HTX M6230 Polyvinyl Chloride Alloy (PVC Alloy)
| Category | Polymer , Thermoplastic , Vinyl (PVC) |
| Manufacturer | PolyOne Corporation |
| Trade Name | Geon™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Geon™ HTX M6230 Polyvinyl Chloride Alloy (PVC Alloy).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.23 g/cc | 1.23 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0020 - 0.0050 cm/cm | 0.0020 - 0.0050 in/in | ASTM D955 |
| Spiral Flow | 73.7 cm | 29.0 in |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 80 | 80 | ASTM D2240 |
| Tensile Strength, Yield | 43.4 MPa | 6290 psi | Type I, 51 mm/min; ASTM D638 |
| Elongation at Break | 15 % | 15 % | Type I, 51 mm/min; ASTM D638 |
| Tensile Modulus | 2.34 GPa | 339 ksi | Type I, 51 mm/min; ASTM D638 |
| Flexural Strength | 75.8 MPa | 11000 psi | ASTM D790 |
| Flexural Modulus | 2.41 GPa | 350 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.18 mm, Temperature 0.000 °C |
0.993 ft-lb/in @Thickness 0.125 in, Temperature 32.0 °F |
Injection Molded; ASTM D256A |
| 1.10 J/cm @Thickness 3.18 mm, Temperature 23.0 °C |
2.06 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 82.2 °C @Thickness 6.35 mm |
180 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 92.2 °C @Thickness 6.35 mm |
198 °F @Thickness 0.250 in |
Annealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 77.8 °C @Thickness 6.35 mm |
172 °F @Thickness 0.250 in |
Unannealed; ASTM D648 |
| 90.0 °C @Thickness 6.35 mm |
194 °F @Thickness 0.250 in |
Annealed; ASTM D648 | |
| UL RTI, Electrical | 50.0 °C | 122 °F | UL 746 |
| UL RTI, Mechanical with Impact | 50.0 °C | 122 °F | UL 746 |
| UL RTI, Mechanical without Impact | 50.0 °C | 122 °F | UL 746 |
| Flammability, UL94 | V-0 @Thickness 1.47 mm |
V-0 @Thickness 0.0579 in |
All Colors |
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
ALL; UL 94 | |
| 5VA @Thickness 1.50 mm |
5VA @Thickness 0.0591 in |
ALL; UL 94 | |
| 5VA @Thickness 1.55 mm |
5VA @Thickness 0.0610 in |
All Colors |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 204 - 210 °C | 399 - 410 °F |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Features | General Purpose | |
| High Flow | ||
| Medium Impact Resistance | ||
| Forms | Pellets | |
| Generic Material | PVC Alloy | |
| Generic Name | Polyvinyl Chloride Alloy (PVC Alloy) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America | ||
| Uses | Appliances | |
| Business Equipment | ||
| Construction Applications | ||
| Electrical/Electronic Applications | ||
| General Purpose | ||
| Telecommunications |
Users viewing this material also viewed the following:
- Pau Tai UNISTAB MS-550 Solid Complex Stabilizer
- Huntsman IROGRAN® A 75 P 4655 N TPU-Polyester
- Garlock 9850 Compressed Carbon Fiber Gasketing, Nitrile Binder
- Momentive Performance Materials Siloprenâ„¢ LSR 2640 LV Liquid Silicone Rubber - Low Volatile / High Tear
- SABIC Innovative Plastics LNP LUBRICOMP DX94375H PC
- Samsung Cheil Industries Starex® TF-0956 HI-PMMA
- Diamond Polymers NPP30-0500 GF30 BLACK HOMOPOLYMER 30% Glass Filled Black Homopolymer Polypropylene
- Covestro Bayblend® KU 1-1446* Polycarbonate + ABS
- Addiplast Addilene H 542 Polypropylene Homopolymer
- 3M Scotch-Weld™ LSB60 Toughened Epoxy Adhesives
Copyright © lookpolymers.com All Rights Reserved