Styron MAGNUMâ„¢ 375 HP Acrylonitrile Butadiene Styrene (ABS) Resin

Category Polymer , Thermoplastic , ABS Polymer
Manufacturer Styron
Trade Name Magnum™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Styron MAGNUMâ„¢ 375 HP Acrylonitrile Butadiene Styrene (ABS) Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Overview: High Heat, Low Gloss, Medium Impact ABS resin for injection molded automotive interior trim applications.Applications: Chrysler-MSDB-191Ford-WSB-M4D690-AGM-GMP.ABS.009Information provided by Styron
Physical Properties Metric English Comments
Density 1.06 g/cc
0.0383 lb/in³
ASTM D792; ISO 1183/B
Apparent Bulk Density 0.680 g/cc
0.0246 lb/in³
ASTM D1895
Linear Mold Shrinkage, Flow 0.0057 cm/cm
0.0057 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0056 cm/cm
0.0056 in/in
ISO 294-4
Melt Flow 2.1 g/10 min

@Load 3.80 kg,
Temperature 230 °C
2.1 g/10 min

@Load 8.38 lb,
Temperature 446 °F
ASTM D1238; ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 47.0 MPa
6820 psi
ISO 527-2
49.0 MPa
7110 psi
51 mm/min; ASTM D638
Elongation at Break 3.5 %
3.5 %
ISO 527-2/50
8.8 %
8.8 %
51 mm/min; ASTM D638
Elongation at Yield 2.9 %
2.9 %
ISO 527-2/50
3.1 %
3.1 %
51 mm/min; ASTM D638
Tensile Modulus 2.30 GPa
334 ksi
51 mm/min; ASTM D638
2.33 GPa
338 ksi
ISO 527-2
Flexural Strength 72.0 MPa
10400 psi
3-point, 2 mm/min; ISO 178
76.5 MPa
11100 psi
Method I (3 point load), 1.3 mm/min; ASTM D790
Flexural Modulus 2.39 GPa
347 ksi
3-point, 2 mm/min; ISO 178
2.41 GPa
350 ksi
Method I (3 point load), 1.3 mm/min; ASTM D790
Izod Impact, Notched 1.30 J/cm

@Temperature -30.0 °C
2.44 ft-lb/in

@Temperature -22.0 °F
ASTM D256
2.20 J/cm

@Temperature 23.0 °C
4.12 ft-lb/in

@Temperature 73.4 °F
ASTM D256
Izod Impact, Notched (ISO) 10.0 kJ/m²

@Temperature -30.0 °C
4.76 ft-lb/in²

@Temperature -22.0 °F
ISO 180/A
25.0 kJ/m²

@Temperature 23.0 °C
11.9 ft-lb/in²

@Temperature 73.4 °F
ISO 180/A
Charpy Impact, Notched 1.10 J/cm²

@Temperature -30.0 °C
5.23 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
2.20 J/cm²

@Temperature 23.0 °C
10.5 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Dart Drop, Total Energy 23.0 J

@Temperature -30.0 °C
17.0 ft-lb

@Temperature -22.0 °F
Peak Energy; ASTM D3763
30.0 J

@Temperature 23.0 °C
22.1 ft-lb

@Temperature 73.4 °F
Peak Energy; ASTM D3763
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 77.0 µm/m-°C

@Temperature -40.0 - 100 °C
42.8 µin/in-°F

@Temperature -40.0 - 212 °F
ASTM E831
CTE, linear, Transverse to Flow 95.0 µm/m-°C

@Temperature -40.0 - 100 °C
52.8 µin/in-°F

@Temperature -40.0 - 212 °F
ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 98.0 °C
208 °F
Unannealed; ISO 75-2/B
99.4 °C
211 °F
Unannealed; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 81.7 °C
179 °F
Unannealed; ASTM D648
83.9 °C
183 °F
Unannealed; ISO 75-2/A
Vicat Softening Point 103 °C

@Load 5.10 kg
217 °F

@Load 11.2 lb
Rate A (50°C/h); ISO 306/B50; ASTM D1525
Flame Spread 30.0 mm/min
1.18 in/min
FMVSS 302
Processing Properties Metric English Comments
Rear Barrel Temperature 238 °C
460 °F
Middle Barrel Temperature 249 °C
480 °F
Front Barrel Temperature 254 °C
489 °F
Nozzle Temperature 249 - 254 °C
480 - 489 °F
Melt Temperature 243 - 271 °C
469 - 520 °F
Drying Temperature 82.0 - 85.0 °C
180 - 185 °F
Dry Time >= 2.00 hour
>= 2.00 hour