- Samsung Cheil Industries Starex® EG-7000 ABS/PET, Unreinforced
Samsung Cheil Industries Starex® EG-7000 ABS/PET, Unreinforced
| Category | Polymer , Thermoplastic , ABS Polymer , ABS/Polyester Alloy , Polyester, TP , Polyethylene Terephthalate (PET) |
| Manufacturer | Samsung, Cheil Industries |
| Trade Name | Starex® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Samsung Cheil Industries Starex® EG-7000 ABS/PET, Unreinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Samsung Cheil Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.10 g/cc | 1.10 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0040 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0040 - 0.0070 in/in @Thickness 0.126 in |
ASTM D955 |
| Melt Flow | 35 g/10 min @Load 10.0 kg, Temperature 250 °C |
35 g/10 min @Load 22.0 lb, Temperature 482 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 95 | 95 | ASTM D785 |
| Tensile Strength, Yield | 38.2 MPa | 5550 psi | 50 mm/min; ASTM D638 |
| Elongation at Break | 40 % | 40 % | 50 mm/min; ASTM D638 |
| Flexural Strength | 55.9 MPa | 8110 psi | 2.8 mm/min; ASTM D790 |
| Flexural Modulus | 1.96 GPa | 284 ksi | 2.8 mm/min; ASTM D790 |
| Izod Impact, Notched | 2.06 J/cm @Thickness 3.17 mm |
3.86 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C @Thickness 6.40 mm |
172 °F @Thickness 0.252 in |
ASTM D648 |
| Vicat Softening Point | 88.0 °C | 190 °F | B/50; ISO R306 |
| Flammability, UL94 | HB @Thickness 1.50 - 3.00 mm |
HB @Thickness 0.0591 - 0.118 in |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Yellow Index | 20 % @Thickness 3.20 mm |
20 % @Thickness 0.126 in |
ASTM D1925 |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Flexible R148CE Polyvinyl Chloride, Flexible (PVC, Flexible)
- PolyOne Edgetek® AT-30GF/000 FDA Acetal-Copolymer, Glass Filled (discontinued **)
- Momentive Performance Materials RTV122 White Adhesive Sealant, General Purpose Paste
- H.C. Starck Amperit® 742.059 Aluminum Oxide-Titanium Oxide 97-3 (Al2O3-TiO2)
- Polyram PlusTek PB320G6 Nylon 6, 30% Glass Fiber, Flame Retardant
- CLAL-MSX NICLAFOR® 1000 TF Quenched/Precipitation Heat Treated, Drawn Copper Alloy
- Aclo Accutech Polypropylene Copolymer CP0437G10CL Glass Reinforced Coupled
- 3M 9019 Double Coated Tapes with Adhesive 300
- 3M 8402 Polyester Tape
Copyright © lookpolymers.com All Rights Reserved