- BASF Polystyrol® 144 C Polystyrene (Europe)
BASF Polystyrol® 144 C Polystyrene (Europe)
| Category | Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Molded, Unreinforced |
| Manufacturer | BASF |
| Trade Name | Polystyrol® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Polystyrol® 144 C Polystyrene (Europe).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Very easy flowing grade, often blended with impact-modified Polystyrol or used as a coextruded glossy layer.Data was collected by ISO methods and provided by BASF.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | |
| Water Absorption | 0.10 % | 0.10 % | |
| Moisture Absorption at Equilibrium | 0.10 % | 0.10 % | |
| Linear Mold Shrinkage, Flow | 0.0045 cm/cm | 0.0045 in/in | |
| Melt Flow | 28 g/10 min @Load 5.00 kg, Temperature 200 °C |
28 g/10 min @Load 11.0 lb, Temperature 392 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 42.0 MPa | 6090 psi | |
| Elongation at Break | 1.5 % | 1.5 % | |
| Tensile Modulus | 3.30 GPa | 479 ksi | |
| Charpy Impact Unnotched | 1.00 J/cm² | 4.76 ft-lb/in² | |
| Charpy Impact, Notched | 0.200 J/cm² | 0.952 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 3100 MPa | 450000 psi | |
| Tensile Creep Modulus, 1000 hours | 2200 MPa | 319000 psi |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 80.0 µm/m-°C @Temperature 20.0 °C |
44.4 µin/in-°F @Temperature 68.0 °F |
|
| Deflection Temperature at 0.46 MPa (66 psi) | 80.0 °C | 176 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | |
| Vicat Softening Point | 84.0 °C | 183 °F | |
| Glass Transition Temp, Tg | 85.0 °C | 185 °F | |
| Flammability, UL94 | HB @Thickness 3.18 mm |
HB @Thickness 0.125 in |
|
| Oxygen Index | 18 % | 18 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Constant | 2.5 @Frequency 100 Hz |
2.5 @Frequency 100 Hz |
|
| 2.5 @Frequency 1e+6 Hz |
2.5 @Frequency 1e+6 Hz |
||
| Dissipation Factor | 0.000070 @Frequency 1e+6 Hz |
0.000070 @Frequency 1e+6 Hz |
|
| 0.000090 @Frequency 100 Hz |
0.000090 @Frequency 100 Hz |
||
| Comparative Tracking Index | 375 V | 375 V |
Users viewing this material also viewed the following:
- Huntsman Araldite AER 4100 N80 Brominated Resin
- Lord Adhesives 7544 Two-Component, Non-Sag, Fast-Cure Urethane Adhesive
- Special Metals INCONEL® 706 Precipitation Hardening Alloy, Forged Disc, 2 Part Heat Treatment
- SCG Chemicals EL-Leneâ„¢ L1810F Linear Low Density Polyethylene Film
- ChevronTexaco Regal® 68 R&O
- DuPont Performance Polymers Crastin® ST820 NC010 Polybutylene Terephthalate (PBT) (Unverified Data**)
- Fainplast Compounds CL 65 Flexible PVC, Sheathing
- BASF Palatinol® 11P-E (DUP) Linear Phthalate
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR Suprex Clay Filler
Copyright © lookpolymers.com All Rights Reserved