- Cossa Polimeri ESTAPROP KUR 1520 TG05 Polypropylene, 10% Mineral Filled
Cossa Polimeri ESTAPROP KUR 1520 TG05 Polypropylene, 10% Mineral Filled
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene Copolymer , Polypropylene, Mineral Reinforced |
| Manufacturer | Cossa Polimeri S.r.L. |
| Trade Name | ESTAPROP |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Cossa Polimeri ESTAPROP KUR 1520 TG05 Polypropylene, 10% Mineral Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
PP copolymer 10% mineral fillerElastomer modified, very high impact strength at low temperatureInformation provided by Cossa Polimeri S.r.l.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ASTM D 792 |
| Linear Mold Shrinkage | 0.012 - 0.015 cm/cm | 0.012 - 0.015 in/in | ASTM D 955 |
| Melt Flow | 15 g/10 min @Load 2.16 kg, Temperature 230 °C |
15 g/10 min @Load 4.76 lb, Temperature 446 °F |
ASTM D 1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 15.0 MPa | 2180 psi | ASTM D 638 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D 638 |
| Tensile Modulus | 1.00 GPa | 145 ksi | ASTM D 638 |
| Flexural Modulus | >= 0.800 GPa | >= 116 ksi | ASTM D 790 |
| Izod Impact, Notched | 1.00 J/cm @Temperature -20.0 °C |
1.87 ft-lb/in @Temperature -4.00 °F |
ASTM D 638 |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ASTM D 256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | >= 50.0 °C @Load 5.00 kg |
>= 122 °F @Load 11.0 lb |
50°C/hr; ASTM D 1525 |
| Flammability, UL94 | HB @Thickness 1.60 mm |
HB @Thickness 0.0630 in |
|
| HB @Thickness 3.20 mm |
HB @Thickness 0.126 in |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® EXL9330P PC COPOLYMER (Asia Pacific)
- Radici Radilon® N66-SRV130 Nylon 66 (discontinued **)
- SABIC Innovative Plastics LNP LUBRICOMP Lexan_WR2210 PC
- Techmer ES Plastiblend® PC/PBT IM 5220 BK
- UBE C (Low-Cis) HIPS (n-DM = 0.03 wt % and PH-3H = 0.03 wt %)
- A. Schulman INVISION™ VX-5065UI Soft Touch Polyolefin Thermoplastic
- Tisan TISOPLEN® 10% Calcite Filled Heat Stabilized Copolymer Polypropylene
- Braskem TI41000WM Impact Copolymer Polypropylene
Copyright © lookpolymers.com All Rights Reserved