PolyOne Edgetek® NN-50GF/000EM L Polyamide 66 (Nylon 66)
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 |
| Manufacturer | PolyOne Corporation |
| Trade Name | Edgetek® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PolyOne Edgetek® NN-50GF/000EM L Polyamide 66 (Nylon 66).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by PolyOne
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.57 g/cc | 1.57 g/cc | ASTM D792 |
| Water Absorption | 0.50 % | 0.50 % | @ 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | ASTM D785 |
| Tensile Strength at Break | 224 MPa | 32500 psi | Type I, 5.1 mm/min; ASTM D638 |
| Elongation at Break | 2.0 % | 2.0 % | Type I, 5.1 mm/min; ASTM D638 |
| Tensile Modulus | 16.5 GPa | 2390 ksi | Type I, 5.1 mm/min; ASTM D638 |
| Flexural Strength | 317 MPa | 46000 psi | ASTM D790 |
| Flexural Modulus | 15.2 GPa | 2200 ksi | ASTM D790 |
| Compressive Strength | 185 MPa | 26800 psi | ASTM D695 |
| Izod Impact, Notched | 1.40 J/cm @Thickness 6.35 mm, Temperature 23.0 °C |
2.62 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F |
Injection Molded; ASTM D256A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 31.0 µm/m-°C | 17.2 µin/in-°F | ASTM D696 |
| Thermal Conductivity | 0.530 W/m-K | 3.68 BTU-in/hr-ft²-°F | ASTM C177 |
| Deflection Temperature at 0.46 MPa (66 psi) | 254 °C @Thickness 3.18 mm |
489 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 254 °C @Thickness 3.18 mm |
489 °F @Thickness 0.125 in |
Annealed; ASTM D648 |
| Flammability, UL94 | HB | HB | UL 94 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | ASTM D257 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 282 - 299 °C | 540 - 570 °F | |
| Mold Temperature | 87.8 - 107 °C | 190 - 225 °F | |
| Drying Temperature | 82.2 - 93.3 °C | 180 - 200 °F | |
| Dry Time | 2.00 hour | 2.00 hour |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Additive | Lubricant | |
| Mold Release | ||
| Features | Lubricated | |
| Filler / Reinforcement | Glass Fiber Reinforcement | |
| Forms | Pellets | |
| Generic Material | Nylon 66 | |
| Generic Name | Polyamide 66 (Nylon 66) | |
| Regional Availability | Africa & Middle East | |
| Asia Pacific | ||
| Europe | ||
| North America | ||
| South America |
Users viewing this material also viewed the following:
- PolyOne Geon™ Vinyl Wire & Cable EHA70L Polyvinyl Chloride, Flexible (PVC, Flexible)
- Proto3000 Objet Digital Materials™ DM_9110/9410/9210/9310 Rubber-like Prototyping Polymer
- ExxonMobil Santoprene® 261-87 Thermoplastic Elastomer (discontinued **)
- LNP ULTEM® UCF1205 Polyetherimide, 12% Carbon Fiber Reinforcement, 5% PTFE Lubricant (discontinued **)
- Cookson Group Plaskon® S-7LA Molding Compound (discontinued **)
- Hexion Bakelite™ PF 13591 Phenolic Formaldehyde Resin, High Surface Quality, UL Listed (discontinued **)
- M. Holland Company PP200 Polypropylene Homopolymer
- Stir SpA A 58 AT (PVC)
- EMS-Grivory Grivory® 1SVX-65H nat PA1010-GF65
- Arkema Group Rilsan® ASR 30 Nylon 12, 30% Carbon Fiber Filled (Conditioned)
Copyright © lookpolymers.com All Rights Reserved