Crucible Steel Aquamet® 19 Stainless Steel

Category Metal , Ferrous Metal , Austenitic , Stainless Steel
Manufacturer Crucible Steel
Trade Name Aquamet®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Crucible Steel Aquamet® 19 Stainless Steel.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AQUAMET 19 is a modified Type 304 stainless steel that is fully austenitic and non-magnetic. Strengthened by adding nitrogen to the melt, it has better corrosion resistance than Type 304 stainless. AQUAMET 19 has proven itself in demanding service on shrimpers, crabbers, scallopers, and other fishing boats as well as on pleasure craft. It may be considered as an economical alternative to AQUAMET 22.Information provided by Crucible Specialty Metals.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 655 MPa

@Thickness 76.2 - 305 mm
95000 psi

@Thickness 3.00 - 12.0 in
896 MPa

@Thickness <=38.1 mm
130000 psi

@Thickness <=1.50 in
Tensile Strength, Yield 345 MPa

@Strain 0.200 %,
Thickness 76.2 - 305 mm
50000 psi

@Strain 0.200 %,
Thickness 3.00 - 12.0 in
Tension
724 MPa

@Strain 0.200 %,
Thickness <=38.1 mm
105000 psi

@Strain 0.200 %,
Thickness <=1.50 in
Tension
Elongation at Break 35 %
35 %
in 2"; 3" to 12"
20 %

@Thickness <=38.1 mm
20 %

@Thickness <=1.50 in
in 2"
Reduction of Area 55 %
55 %
Shear Strength 228 MPa

@Strain 0.200 %,
Thickness 76.2 - 305 mm
33000 psi

@Strain 0.200 %,
Thickness 3.00 - 12.0 in
483 MPa

@Strain 0.200 %,
Thickness <=38.1 mm
70000 psi

@Strain 0.200 %,
Thickness <=1.50 in
Component Elements Properties Metric English Comments
Carbon, C <= 0.080 %
<= 0.080 %
Chromium, Cr 18 - 20 %
18 - 20 %
Iron, Fe >= 66.05 %
>= 66.05 %
As Remainder
Manganese, Mn <= 2.0 %
<= 2.0 %
Nickel, Ni 8.0 - 10.5 %
8.0 - 10.5 %
Nitrogen, N 0.20 - 0.30 %
0.20 - 0.30 %
Phosphorous, P <= 0.040 %
<= 0.040 %
Silicon, Si <= 1.0 %
<= 1.0 %
Sulfur, S <= 0.030 %
<= 0.030 %