Polimeri Europa KOBLEND PCA 51 PC+ABS (discontinued **)

Category	Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Polimeri Europa KOBLEND PCA 51 PC+ABS (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Symbol according to ISO 1043/1: PC+ABS Injection moulding grade with flame retardant properties ( UL 94 V-0 at 1.6mm thickness ) and good light resistance. Vicat/B50 = 90°C Main application fields: business machines, electronic and electrical industryUnfilled. Suitable for Injection Molding. Supplied as pellets.ISO data. Information provided by EnichemPolimeri Europa now has Enichem's plastics businesses. This grade is no longer in the product line.

Physical Properties	Metric	English	Comments
Density	1.17 g/cc	0.0423 lb/in³
Water Absorption	0.60 %	0.60 %
Melt Flow	21 g/10 min @Load 5.00 kg, Temperature 250 °C	21 g/10 min @Load 11.0 lb, Temperature 482 °F	cm³/10 min

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	54.0 MPa	7830 psi	50 mm/min
Elongation at Break	>= 50 %	>= 50 %	Nominal
Elongation at Yield	3.6 %	3.6 %	50 mm/min
Tensile Modulus	2.60 GPa	377 ksi	1 mm/min
Izod Impact, Unnotched	NB	NB
	NB @Temperature -30.0 °C	NB @Temperature -22.0 °F
Izod Impact, Notched (ISO)	12.0 kJ/m² @Temperature -30.0 °C	5.71 ft-lb/in² @Temperature -22.0 °F

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	70.0 µm/m-°C @Temperature 20.0 °C	38.9 µin/in-°F @Temperature 68.0 °F
Deflection Temperature at 0.46 MPa (66 psi)	94.0 °C	201 °F
Deflection Temperature at 1.8 MPa (264 psi)	84.0 °C	183 °F
Vicat Softening Point	94.0 °C	201 °F	50°C/hr; 50N
Flammability, UL94	V-0 @Thickness 1.62 mm	V-0 @Thickness 0.0638 in

Electrical Properties	Metric	English
Electrical Resistivity	>= 1.00e+15 ohm-cm	>= 1.00e+15 ohm-cm
Surface Resistance	1.00e+14 ohm	1.00e+14 ohm
Dielectric Constant	2.9 @Frequency 1e+6 Hz	2.9 @Frequency 1e+6 Hz
	3.0 @Frequency 100 Hz	3.0 @Frequency 100 Hz
Dielectric Strength	30.0 kV/mm	762 kV/in
Dissipation Factor	0.0050 @Frequency 100 Hz	0.0050 @Frequency 100 Hz
	0.0070 @Frequency 1e+6 Hz	0.0070 @Frequency 1e+6 Hz
Comparative Tracking Index	300 V	300 V