Supreme Petrochem SH 03 High Impact Polystyrene

Category	Polymer , Thermoplastic , Polystyrene (PS) , Polystyrene, Impact Modified
Manufacturer	Supreme Petrochem LTD
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Supreme Petrochem SH 03 High Impact Polystyrene.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Characteristics High flow Good melt strength Excellent toughness Processing MoldingApplications Gas assisted injection molding of T.V. cabinets Suitable for thin walled parts, AC grills and toys Base material for compoundingMaterial Status: Commercial : ActiveAgency Ratings: FDA 21 CFR 177.1640, UL file E185934Information provided by Supreme Petrochem LTD

Physical Properties	Metric	English	Comments
Specific Gravity	1.03 g/cc	1.03 g/cc	ASTM D792
Melt Flow	10 g/10 min @Load 5.00 kg, Temperature 200 Â°C	10 g/10 min @Load 11.0 lb, Temperature 392 Â°F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	21.6 MPa	3130 psi	50 mm/min; ASTM D638
Elongation at Break	50 %	50 %	50 mm/min; ASTM D638
Flexural Strength	36.3 MPa @Thickness 3.20 mm	5260 psi @Thickness 0.126 in	ASTM D790
Flexural Modulus	1.77 GPa @Thickness 3.20 mm	256 ksi @Thickness 0.126 in	ASTM D790
Izod Impact, Notched	1.00 J/cm @Thickness 3.20 mm	1.87 ft-lb/in @Thickness 0.126 in	ASTM D256

Thermal Properties	Metric	English	Comments
Deflection Temperature at 1.8 MPa (264 psi)	76.0 Â°C	169 Â°F	ASTM D648
Vicat Softening Point	97.0 Â°C	207 Â°F	1kg / 120Â°C; ASTM D1525
Flammability, UL94	HB @Thickness 1.60 mm	HB @Thickness 0.0630 in

Processing Properties	Metric	English	Comments
Melt Temperature	180 - 260 Â°C	356 - 500 Â°F
Mold Temperature	40.0 - 60.0 Â°C	104 - 140 Â°F