Nilit RECONYL A H Recycled nylon 6.6 for injection molding
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit RECONYL A H Recycled nylon 6.6 for injection molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recycled nylon 6.6 for injection molding, heat stabilized (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 |
| Water Absorption | 2.3 - 3.2 % | 2.3 - 3.2 % | ISO 62 |
| Water Absorption at Saturation | 7.5 - 8.5 % | 7.5 - 8.5 % | ISO 62 |
| Linear Mold Shrinkage | 0.014 - 0.024 cm/cm | 0.014 - 0.024 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 145 MPa | 21000 psi | ISO 2039-1 |
| Tensile Strength at Break | 95.0 MPa | 13800 psi | ISO 527 |
| Elongation at Break | 8.0 % | 8.0 % | ISO 527 |
| Tensile Modulus | 3.30 GPa | 479 ksi | ISO 527 |
| Flexural Strength | 100 MPa | 14500 psi | ISO 178 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ISO 178 |
| Charpy Impact Unnotched | 5.50 J/cm² | 26.2 ft-lb/in² | DIN 53453 |
| 4.00 J/cm² @Temperature -40.0 °C |
19.0 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.300 J/cm² | 1.43 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 256 °C | 493 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 90.0 °C | 194 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 100 °C | 212 °F | ISO 75 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Lexan® HPS2S PC (Europe-Africa-Middle East)
- REXtac Rextac® RT 2880 Amorphous Polyalphaolefin (APAO)
- Rogers Corporation Bisco™ FPC Cellular Silicone Foam
- Greene Tweed Arlon® 1163 PEEK, Glass Filled
- Momentive Performance Materials TSE399 Translucent Adhesive Sealant, Flowable
- SABIC Innovative Plastics LNP STAT-KON 9X02785 PC
- SABIC Innovative Plastics LNP STAT-KON RE0029 PA 66
- Dow LDPE 5004I Low Density Polyethylene, Extrusion Coating Grade
- Sumitomo Bakelite North America FS-10-VO-200-P Short-Glass Reinforced Diallyl Phthalate
- Henkel Hysol MA 562SFR Core Splice Adhesive
Copyright © lookpolymers.com All Rights Reserved