- PlastiComp Complet® LCF40 - TPU Rigid Thermoplastic Polyurethane, 40% Long Carbon Fiber Reinforced
PlastiComp Complet® LCF40 - TPU Rigid Thermoplastic Polyurethane, 40% Long Carbon Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyurethane, TP , Thermoplastic Polyurethane (TPUR), Carbon Fiber Reinforced |
| Manufacturer | PlastiComp |
| Trade Name | Complēt® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PlastiComp Complet® LCF40 - TPU Rigid Thermoplastic Polyurethane, 40% Long Carbon Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Complēt® long-fiber reinforced pellets are manufactured to exceed expectation for quality and performance.Polyurethane with 40% carbon fiber reinforcementInformation provided by PlastiComp, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.38 g/cc | 1.38 g/cc | ASTM D-792 |
| Filler Content | 40 % | 40 % | Carbon Fiber |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength | 262 MPa | 38000 psi | ASTM D-638 |
| Elongation at Break | 1.0 - 2.0 % | 1.0 - 2.0 % | ASTM D-638 |
| Tensile Modulus | 28.966 GPa | 4201.2 ksi | ASTM D-638 |
| Flexural Strength | 428 MPa | 62100 psi | ASTM D-790 |
| Flexural Modulus | 28.276 GPa | 4101.1 ksi | ASTM D-790 |
| Izod Impact, Notched | 2.94 J/cm | 5.51 ft-lb/in | ASTM D-256 |
| Izod Impact, Unnotched | 11.214 J/cm | 21.008 ft-lb/in | ASTM D-4812 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | ASTM D-648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 204 - 227 °C | 400 - 440 °F | |
| Middle Barrel Temperature | 210 - 232 °C | 410 - 450 °F | |
| Front Barrel Temperature | 216 - 238 °C | 420 - 460 °F | |
| Nozzle Temperature | 221 - 243 °C | 430 - 470 °F | |
| Melt Temperature | 216 - 238 °C | 420 - 460 °F | |
| Mold Temperature | 87.8 °C | 190 °F | |
| Injection Velocity | 50.8 - 76.2 mm/sec | 2.00 - 3.00 in/sec | |
| Drying Temperature | 88.0 °C @Time 14400 sec |
190 °F @Time 4.00 hour |
|
| Moisture Content | <= 0.020 % | <= 0.020 % | |
| Back Pressure | 0.172 - 0.345 MPa | 25.0 - 50.0 psi | |
| Cushion | 0.635 cm | 0.250 in | |
| Screw Speed | 30 - 50 rpm | 30 - 50 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Pressure | Medium to maximum |
Users viewing this material also viewed the following:
- Plastcom SLOVALEN PC 79 GF 20 PP, 20% glass fibre, mod. of mech. prop.
- EVALCA EVAL® EP-F104BW Ethylene Vinyl Alcohol Copolymer Resin (discontinued **)
- DSM Akulon® Ultraflow™ K-FKGS6 Nylon 6-30% Glass Reinforced (European and Asian Grade) (Cond) (discontinued *
- Latrobe CM-52â„¢ ASTM M52 High Speed Steel
- Stir SpA Giesse IPM/6Z (PVC)
- Samsung Cheil Industries Infino® UF-1013 PC, Unreinforced FR
- Toyobo Vylopet® EMC130-04 Glass Reinforced Polyester, Easy Molding Grade
- DuPont Teijin Films Mylar® EB31 Polyester Film, 200 Gauge
- China Tungsten YG15 Cemented Tungsten Carbide for Mining Purposes
- ArcelorMittal 57 High formability steel for drawing, Cold rolled
Copyright © lookpolymers.com All Rights Reserved