- PTS Trimid® N6-615I-NC Extrusion Grade Nylon 6
PTS Trimid® N6-615I-NC Extrusion Grade Nylon 6
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Extruded |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trimid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trimid® N6-615I-NC Extrusion Grade Nylon 6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Total Extractables < 1.5.Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ASTM D792 |
| Viscosity Measurement | 100 | 100 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 79.3 MPa | 11500 psi | ASTM D638 |
| Tensile Strength, Yield | 75.8 MPa | 11000 psi | ASTM D638 |
| Elongation at Break | 250 % | 250 % | ASTM D638 |
| Flexural Modulus | 2.93 GPa | 425 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm @Thickness 3.17 mm |
0.899 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 130 °C | 266 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | <= 216 °C | <= 420 °F | |
| Middle Barrel Temperature | 227 - 254 °C | 440 - 490 °F | |
| Front Barrel Temperature | 238 - 266 °C | 460 - 510 °F | |
| Nozzle Temperature | 238 - 266 °C | 460 - 510 °F | |
| Melt Temperature | 232 - 271 °C | 450 - 520 °F | |
| Mold Temperature | 21.1 - 93.3 °C | 70.0 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Injection Pressure | 82.7 - 172 MPa | 12000 - 25000 psi | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm |
Users viewing this material also viewed the following:
- LG Chemical BM662 ABS, Heat Resistance
- Gwent Electronic Materials P2121112P3 Tetrafluoromethane Plasma Modified Graphene Nanoplatelets
- Solvay TECHNYL® A 218 V35 PA66, 35% glass fiber, DRY
- Taiwan PU Corporation TPU-BH90 Hydrolysis Resistance, Blow Molding Polyether Base TPU
- Solvay ALKAMULS® A Surfactant
- Unitika M1030B PA6, Dry
- Addiplast Addilene H 490 M20S Flame Retardant Polypropylene, 20% Mineral Filled
- ATI Allegheny Ludlum Type 310L Stainless Steel
- 3M N-200J Adhesion Promoter
Copyright © lookpolymers.com All Rights Reserved