Plastcom SLOVAMID 6 HI Polyamide 6, Impacted

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Impact Grade
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID 6 HI Polyamide 6, Impacted.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesPA 6 with the content of thermoplastic elastomer. Impacted, for mouldings with high toughness either at low temperatures, suitable for external use, eg. ski shoes, sports and safety helmets, protection ledges of the car-doors. Delivered in natural and in the full RAL color scale.Application: Injection MouldingInformation Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.08 g/cc
0.0390 lb/in³
STN 64 0111
Linear Mold Shrinkage 0.0208 cm/cm
0.0208 in/in
STN 64 0808
Linear Mold Shrinkage, Transverse 0.0204 cm/cm
0.0204 in/in
STN 64 0808
Melt Flow 5.0 g/10 min

@Load 2.16 kg,
Temperature 230 °C
5.0 g/10 min

@Load 4.76 lb,
Temperature 446 °F
STN EN ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 58.0 MPa
8410 psi
STN EN ISO 527-2
Elongation at Break 4.0 %
4.0 %
STN EN ISO 527-2
Tensile Modulus 2.25 GPa
326 ksi
STN EN ISO 527-2
Flexural Strength 73.0 MPa
10600 psi
STN EN ISO 178
Flexural Modulus 1.93 GPa
280 ksi
STN EN ISO 178
Charpy Impact Unnotched NB

@Temperature 23.0 °C
NB

@Temperature 73.4 °F
STN EN ISO 179
NB

@Temperature -20.0 °C
NB

@Temperature -4.00 °F
STN EN ISO 179
Charpy Impact, Notched 1.00 J/cm²

@Temperature -20.0 °C
4.76 ft-lb/in²

@Temperature -4.00 °F
STN EN ISO 179
2.40 J/cm²

@Temperature 23.0 °C
11.4 ft-lb/in²

@Temperature 73.4 °F
STN EN ISO 179
Thermal Properties Metric English Comments
Melting Point 220 °C
428 °F
DSC; STN EN ISO 3146
Deflection Temperature at 1.8 MPa (264 psi) 55.0 °C
131 °F
STN EN ISO 75/A
Vicat Softening Point 179 °C
354 °F
B; STN EN ISO 306
Flammability, UL94 HB
HB
Glow Wire Test 850 °C
1560 °F
STN IEC 60695-2-10
Processing Properties Metric English Comments
Melt Temperature 240 - 260 °C
464 - 500 °F
Mold Temperature 50.0 - 60.0 °C
122 - 140 °F
Drying Temperature 80.0 °C
176 °F
Dry Time 4 hour
4 hour
Moisture Content 0.15 %
0.15 %
STN EN ISO 960
Injection Pressure 80.0 - 150 MPa
11600 - 21800 psi