Plastcom SLOVAMID 6 GF 65 PA6, 65% glass fibre

Category Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 60% Glass Fiber Filled
Manufacturer Plastcom spol. s r.o.
Trade Name SLOVAMID 6
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Plastcom SLOVAMID 6 GF 65 PA6, 65% glass fibre.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FeaturesPA 6 for injection moulding, chemically strengthened with 65% of glass fibre, for mouldings with high strength and toughness used in the automotive, electrical, engineering and consumer-goods industry. Application: grips of electrotools, hobby tools, gears, covers of electric appliances, cooling skrews of blowers, electromotors, carrying parts in the automotive industry. Replacement of metal parts from ZAMAC and etc.Delivered in natural mode and in black.Packaging, transport, stockingThe product is packed in hermetically closed thick-walled 25 kg PE bags, on a 1.000 kg palette coated in a stretch foil, in big bags with a thick PE foil fixed on a 1.000 kg palette, in paper octabins with a thick PE foil fixed on a 1.000 kg palette or in other packaging according to customer requirements. The transport is provided in closed-up vehicles where the material is protected against movement and mechanical damage. The product requires stocking in closed-up, dry places protected against sun and thermal radiation.Information Provided by Plastcom spol. s r.o.
Physical Properties Metric English Comments
Density 1.71 g/cc
0.0618 lb/in³
Viscosity Measurement 0.27 - 0.41
0.27 - 0.41
Linear Mold Shrinkage 0.0027 cm/cm
0.0027 in/in
Linear Mold Shrinkage, Transverse 0.0041 cm/cm
0.0041 in/in
Melt Flow 5.0 g/10 min

@Load 0.325 kg,
Temperature 270 °C
5.0 g/10 min

@Load 0.716 lb,
Temperature 518 °F
Mechanical Properties Metric English Comments
Tensile Strength at Break 235 MPa
34100 psi
Elongation at Break 2.5 %
2.5 %
Tensile Modulus 19.2 GPa
2780 ksi
Flexural Strength 325 MPa
47100 psi
Flexural Modulus 16.45 GPa
2386 ksi
Charpy Impact Unnotched 9.00 J/cm²

@Temperature 23.0 °C
42.8 ft-lb/in²

@Temperature 73.4 °F
9.00 J/cm²

@Temperature -20.0 °C
42.8 ft-lb/in²

@Temperature -4.00 °F
Charpy Impact, Notched 1.80 J/cm²

@Temperature -20.0 °C
8.57 ft-lb/in²

@Temperature -4.00 °F
2.50 J/cm²

@Temperature 23.0 °C
11.9 ft-lb/in²

@Temperature 73.4 °F
Thermal Properties Metric English Comments
Melting Point 222 °C
432 °F
Deflection Temperature at 1.8 MPa (264 psi) 215 °C
419 °F
Vicat Softening Point 215 °C
419 °F
B
Flammability, UL94 HB
HB
Glow Wire Test 650 °C
1200 °F
Electrical Properties Metric English Comments
Volume Resistivity 6.00e+12 ohm-cm
6.00e+12 ohm-cm
Dielectric Strength 33.0 kV/mm
838 kV/in
Comparative Tracking Index 600 V
600 V
Processing Properties Metric English Comments
Melt Temperature 270 - 300 °C
518 - 572 °F
Mold Temperature 90.0 - 100 °C
194 - 212 °F
Drying Temperature 90.0 °C
194 °F
Dry Time 4 hour
4 hour
Moisture Content 0.10 %
0.10 %
Injection Pressure 90.0 - 150 MPa
13100 - 21800 psi