Plastcom SLOVALEN PH 49 GF 30 003/3M Polypropylene reinforced with glass fiber, heat stabilized
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Glass Fiber Filler |
| Manufacturer | Plastcom spol. s r.o. |
| Trade Name | SLOVALEN |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Plastcom SLOVALEN PH 49 GF 30 003/3M Polypropylene reinforced with glass fiber, heat stabilized.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Modified homopolymer PP for injection molding, reinforced with 30% glass fiber, heat stabilized. Delivered in black color.Information Provided by Plastcom spol. s r.o.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | STN EN ISO 1183-1 |
| Filler Content | 30 % | 30 % | |
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | STN EN ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.0128 cm/cm | 0.0128 in/in | STN EN ISO 294-4 |
| Melt Flow | 3.0 g/10 min @Load 2.16 kg, Temperature 230 °C |
3.0 g/10 min @Load 4.76 lb, Temperature 446 °F |
STN EN ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 95.0 MPa | 13800 psi | STN EN ISO 527-2 |
| Elongation at Break | 2.0 % | 2.0 % | STN EN ISO 527-2 |
| Tensile Modulus | 7.20 GPa | 1040 ksi | STN EN ISO 527-2 |
| Flexural Strength | 135 MPa | 19600 psi | STN EN ISO 178 |
| Flexural Modulus | 5.70 GPa | 827 ksi | STN EN ISO 178 |
| Charpy Impact Unnotched | 5.20 J/cm² @Temperature -20.0 °C |
24.7 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 5.50 J/cm² @Temperature 23.0 °C |
26.2 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 | |
| Charpy Impact, Notched | 0.900 J/cm² @Temperature -20.0 °C |
4.28 ft-lb/in² @Temperature -4.00 °F |
STN EN ISO 179 |
| 1.20 J/cm² @Temperature 23.0 °C |
5.71 ft-lb/in² @Temperature 73.4 °F |
STN EN ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 160 °C | 320 °F | STN EN 11357-1 |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | STN EN ISO 75-2 (A) |
| Vicat Softening Point | 155 °C | 311 °F | STN EN ISO 306 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 200 - 250 °C | 392 - 482 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Drying Temperature | 80.0 °C @Time 14400 sec |
176 °F @Time 4.00 hour |
|
| Injection Pressure | 70.0 - 120 MPa | 10200 - 17400 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | Black |
Users viewing this material also viewed the following:
- Nye Lubricants 737 (RL) Synthetic Oil
- Okulen® 2000 PE-UHMW, W
- A. Schulman PP 1817-01 Polypropylene Utility Grade Random Co-Polymer
- ExxonMobil PP7011L1 Polypropylene Impact Copolymer
- Chosun Refractories C18B Magnesia Carbon Brick for Converter
- Chosun Refractories LW-23 Special Insulating Firebrick
- Arkema Group Rilsan® AMN G8 TLD Nylon 12, Graphite Filled (Conditioned)
- Asahi Glass Lumiflon LF-200 Solvent Soluble Fluoropolymer w/ Melamine hardening agent
- Radici Radiflam® B RV250AE Polybutylene Terephthalate - 25% Glass fiber reinforced
- Beijing Ranger Chem SM-602RX75 Solvent Based Epoxy Resin
Copyright © lookpolymers.com All Rights Reserved