Petromont 1002 High Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , HDPE
Manufacturer Petromont
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Petromont 1002 High Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Petromont HDPE 1002 is a blow moulding high-density polyethylene copolymer resin produced using the UNIPOL® Process. This multi-purpose resin can be used on intermittent and continuous extrusion blow moulding machines to produce containers up to 10 litres for use in various packaging applications. The glossy appearance that is characteristic of Pétromont`s resins results in parts with good surface quality.Combining its low melt index and high density, Petromont HDPE 1002 exhibits excellent rigidity and top load performance while maintaining outstanding drop impact properties and excellent environmental stress cracking properties. The specially designed formulation makes Petromont HDPE 1002 less susceptible to degradation during processing. This product is also Anti-static modified.
Physical Properties Metric English Comments
Density 0.955 g/cc
0.0345 lb/in³
ASTM D1505
ESCR 100% Igepal® 33 hour
33 hour
F<sub>50</sub>; ASTM D1693-B
Melt Flow 0.33 g/10 min
0.33 g/10 min
I<sub>2</sub>; ASTM D1238
29 g/10 min
29 g/10 min
I<sub>21</sub>; ASTM D238
Mechanical Properties Metric English Comments
Hardness, Shore D 67
67
ASTM D2240
Tensile Strength, Yield 26.9 MPa
3900 psi
ASTM D638
Elongation at Break >= 800 %
>= 800 %
ASTM D638
Flexural Modulus 1.325 GPa
192.2 ksi
ASTM D790
Izod Impact, Notched 1.60 J/cm
3.00 ft-lb/in
ASTM D256
Thermal Properties Metric English Comments
CTE, linear 130 µm/m-°C

@Temperature 20.0 °C
72.2 µin/in-°F

@Temperature 68.0 °F
ASTM D696
Melting Point 134 °C
273 °F
Petromont
Crystallization Temperature 111 °C
232 °F
Petromont
Deflection Temperature at 0.46 MPa (66 psi) 74.0 °C
165 °F
ASTM D648
Vicat Softening Point 128 °C
262 °F
ASTM D1525
Brittleness Temperature <= -76.0 °C
<= -105 °F
ASTM D746
Descriptive Properties Value Comments
Process Blow Molding