PTS Trimid® N66-G13L 13% Glass Fiber Reinforced Lubed Nylon 6/6
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 10% Glass Fiber Filled |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trimid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trimid® N66-G13L 13% Glass Fiber Reinforced Lubed Nylon 6/6.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.22 g/cc | 0.0441 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 117 MPa @Thickness 3.17 mm |
17000 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.17 mm |
3.0 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Modulus | 6.80 GPa @Thickness 3.17 mm |
986 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 0.900 J/cm @Thickness 3.17 mm |
1.69 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 254 °C | 489 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 243 °C | 469 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 254 °C | 490 °F | |
| Middle Barrel Temperature | 268 °C | 515 °F | |
| Front Barrel Temperature | 285 °C | 545 °F | |
| Nozzle Temperature | 266 - 282 °C | 510 - 540 °F | |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 26.7 - 93.3 °C | 80.0 - 200 °F | |
| Drying Temperature | 71.1 °C | 160 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 68.9 MPa | 10000 psi | |
| Back Pressure | 0.0689 - 0.689 MPa | 10.0 - 100 psi | |
| Screw Speed | 30 - 60 rpm | 30 - 60 rpm |
Users viewing this material also viewed the following:
- Mallard Creek Polymers Rovene® 6506 Styrene-Acrylic Emulsion
- Lehmann & Voss LUVOCOM® 1850-7487 PBT, with carbon fiber
- Haynes 242® alloy, cold rolled sheet, annealed and aged
- Teknor Apex Sinvicomp SRF 3705 Polyvinyl Chloride, Rigid
- UBE 5034FDX33 Air Blown Nylon 6/66 Film
- Polyplastics FR-PET® B9030 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Slow burning, General purpose
- Constellium Alumold® 400 Aluminum
- Arlon R37642R062 0.062" (1.57 mm) Cured Silicone Rubber with PTFE Coated Fiberglass Carrier
- Solvay Specialty Polymers Veradel® 3000RP Polyethersulfone (PESU) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved