Polymer Property : Tensile Strength, Ultimate = 17000 psi Product List

Mechanical Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 117 MPa
17000 psi
ASTM D638
Nylene® Vexel™ B12GF30 , 30% Glass Reinforced PBT
Description: Vexel™ B12GF30 is a 30% glass fiber reinforced, general purpose PBT. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all operting companies of Polymeri..
Tensile Strength, Ultimate 117 MPa
17000 psi
ASTM D638
Nylene® Vexel™ B12GF30 FR , 30% Glass Reinforced, Flame Retardant PBT
Description: Vexel™ B12GF30 FR is a 30% glass fiber reinforced, flame retardant PBT. B12GF30 FR is UL approved. Information provided by Custom Resins. ALM, Nylene Canada, and Custom Resins are all ..
Tensile Strength, Ultimate 117 MPa

@Thickness 3.17 mm
17000 psi

@Thickness 0.125 in
ASTM D638
PTS Trimid® N66-G13L 13% Glass Fiber Reinforced Lubed Nylon 6/6
Information provided by Polymer Technology and Services, LLC (PTS).
Tensile Strength, Ultimate 117 - 186 MPa
17000 - 27000 psi
Average value: 158 MPa Grade Count:17
Overview of materials for Polyetherimide (PEI), 30% Glass Fiber
This property data is a summary of similar materials in the MatWeb database for the category "Polyetherimide, 30% Glass Fiber". Specific grades with glass content between 25% and 34% are included. E..
Tensile Strength, Ultimate 117 MPa
17000 psi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Edgetek® NJ-30GF/000 Nylon 12, Glass Filled  (discontinued **)
Description/Features:Glass Fiber ReinforcedInformation provided by PolyOne Corporation.
Tensile Strength, Ultimate 117 MPa
17000 psi
ASTM D638
IDI Composites A-207 Thermoset Polyester, Sheet
AUTOMOTIVE - Versatile family of compounds specifically designed for automotive structural applications. Low shrink characteristics, heat resistance, long-term dimensional stability, and corrosion r..
Tensile Strength, Ultimate 117.2 MPa
17000 psi
Indium Corp. Indalloy® 209 Sn-Ag-Sb Solder Alloy
Low temperature die attach alloy. Has very high tensile strength. Old Motorola die attach solder; very brittle.Information provided by the manufacturer, Indium Corporation.
Tensile Strength, Ultimate 117 MPa
17000 psi
Haysite HCR-197 Corrosion Resistant Polyester/Glass Sheet
A fiber glass reinforced thermoset polyester sheet using ATLAC® 382 Bisphenol-A Fumarate in the resin matrix. Standard color is light yellow. Additional data covering resistance to specific chemi..
Tensile Strength, Ultimate 117 MPa
17000 psi
ASTM D638
Techmer ES Electrafil® J-50/CF/30/TF/15 Polycarbonate, 30% Carbon Fiber Reinforced, PTFE Lubed
Carbon Fiber Reinforced, PTFE Lubricated
Tensile Strength, Ultimate 117 MPa

@Temperature 704 °C
17000 psi

@Temperature 1300 °F
Crucible Steel 446 Chromium Steel
Crucible 446 is a non-hardenable chromium steel which has the highest corrosion and heat resisting properties of the straight chromium steels. This grade is magnetic at all times. Information provi..
Tensile Strength, Ultimate 117 MPa
17000 psi
ASTM D638
Adell BR-14 Nylon 6, 20% Glass Reinforced
Data provided by Adell Plastics, Inc.
Tensile Strength, Ultimate 117 MPa
17000 psi
ATSM D638
Ashley Polymers Ashlene® 630-13G Nylon 6, 13% Glass Reinforced
A 13% glass fiber reinforced Nylon 6, designed to provide a high flexural modulus and good dimensional stability, while maintaining the ease of processing associated with Nylon 6 type materials.Data..
Tensile Strength, Ultimate 117 MPa
17000 psi
ASTM D638
A. Schulman ComAlloy Hiloy® 513 Polycarbonate, Glass Reinforced, UL
Data provided by the manufacturer, ComAlloy International Company.30% Glass Reinforced.The ComAlloy product line has been integrated into the A Schulman product line.
Tensile Strength, Ultimate 117 MPa
17000 psi
5mm/min; ISO 527
BASF Ultradur B 4406 G4 Q113 20% Glass Filled PBT
Ultradur B4406 G4 Q113 is an UL V0 injection molding PBT grade with 20% glass fiber reinforcement.
Tensile Strength, Ultimate 117 MPa
17000 psi
ATSM D638
Ashley Polymers Ashlene® 1430 Polycarbonate, 30% Glass Reinforced
A 30% glass reinforced polycarbonate for increased mechanical strength and thermal properties. Also available with UV stabilizer. 1433: with UV stabilizer; 1433-H2: with improved UV stabilizer.Dat..
Tensile Strength, Ultimate 117 - 280 MPa
17000 - 40600 psi
Average value: 151 MPa Grade Count:11
Overview of materials for Polypropylene with 60% Glass Fiber Filler
This property data is a summary of similar materials in the MatWeb database for the category "Polypropylene with 60% Glass Fiber Filler". Specific grades with glass content between 55% and 64% are i..
Tensile Strength, Ultimate 117 MPa
17000 psi
Type 1 - Rigids, 0.2 in/min; ASTM D638
PolyOne Lubri-Tech™ PS-30GF/10T2S Polybutylene Terephthalate (PBT), Glass Filled, PTFE/Silicone Lubricated  (d
Description/Features:Glass Fiber ReinforcedPTFE/Silicone LubricatedPolyOne First ChoiceInformation provided by PolyOne Corporation.