PTS Trimid® N6-G15L 15% GFR Nylon 6 with Lube
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, 20% Glass Fiber Filled |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trimid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trimid® N6-G15L 15% GFR Nylon 6 with Lube.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | ASTM D570 |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 120.1 MPa | 17420 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Yield Strength | 164.8 MPa | 23900 psi | ASTM D790 |
| Flexural Modulus | 4.56 GPa | 661 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm @Thickness 3.17 mm |
1.29 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 216 °C | 421 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 199 °C | 390 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | <= 216 °C | <= 420 °F | |
| Middle Barrel Temperature | 227 - 254 °C | 440 - 490 °F | |
| Front Barrel Temperature | 238 - 266 °C | 460 - 510 °F | |
| Nozzle Temperature | 238 - 266 °C | 460 - 510 °F | |
| Melt Temperature | 232 - 271 °C | 450 - 520 °F | |
| Mold Temperature | 21.1 - 93.3 °C | 70.0 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Injection Pressure | 82.7 - 172 MPa | 12000 - 25000 psi | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm |
Users viewing this material also viewed the following:
- RheTech Products GC30P200-00 30% Glass Fiber Reinforced Polypropylene Copolymer, Chemically Coupled, Natural
- Pyrotek A-5C Fiberglass Fabric
- Chevron Phillips Ryton® PR27 Polyphenylene Sulfide Resin (discontinued **)
- H.C. Starck Ampersint® MAP FeNi 50/50 For Hardmetals
- Haynes Hastelloy® G-30® alloy, plate and bar
- Schott Glass 8688 Borosilicate Glass
- Goodfellow E-glass/Epoxy Composite
- 3M 6146 Kraft Medium Duty Reinforced Water Activated Tape
- Ashley Polymers Ashlene® 980LS-43GB Nylon 612, 43% Glass Reinforced
Copyright © lookpolymers.com All Rights Reserved