SABIC Innovative Plastics LNP Thermocomp FF001 PE (Europe-Africa-Middle East)
| Category | Polymer , Thermoplastic , Polyethylene (PE) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP THERMOCOMP |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP Thermocomp FF001 PE (Europe-Africa-Middle East).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* THERMOCOMP* FF001 is a compound based on Polyethylene resin containing Glass Fiber.This data was supplied by SABIC-IP for the Europe-Africa-Middle East region.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 g/cc | 0.0361 lb/in³ | ISO 1183 |
| Moisture Absorption at Equilibrium | 0.00 % | 0.00 % | 23°C / 50% RH; ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0070 cm/cm | 0.0070 in/in | SABIC Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 28.0 MPa | 4060 psi | 5 mm/min; ISO 527 |
| Elongation at Yield | 3.6 % | 3.6 % | 5 mm/min; ISO 527 |
| Tensile Modulus | 1.70 GPa | 247 ksi | 1 mm/min; ISO 527 |
| Flexural Yield Strength | 36.0 MPa | 5220 psi | 2 mm/min; ISO 178 |
| Flexural Modulus | 1.50 GPa | 218 ksi | 2 mm/min; ISO 178 |
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature 23.0 °C |
2.38 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 25.0 kJ/m² @Temperature 23.0 °C |
11.9 ft-lb/in² @Temperature 73.4 °F |
80*10*4; ISO 180/1U |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 62.0 °C | 144 °F | Flatw 80*10*4 sp=64mm; ISO 75/Af |
Users viewing this material also viewed the following:
- Osprey Metals 90/10 Cu Sn Powder (Grade 95% - 16)
- Kazanorgsintez 102-15 Composition of Low Density Polyethylene, Crack-Proof
- Grupo Repol Dinalon® B1S25 G25 H PA6 25% Glass Fiber, Heat Stabilized
- Taiwan Sheen Soon Sheenthane® AH-573 TPU for Hotmelt Adhesive
- Unitika AX-1500W Conditioned
- China Tungsten YT14 Tungsten Carbide for Cutting Tools
- Ashley Polymers Ashlene® 925L-25G Nylon 12, 25% Glass Reinforced
- ATI Allegheny Ludlum AL 17-4 High Strength Stainless Steel, UNS S17400
- 3M Tartan™ 302 Box Sealing Tape
Copyright © lookpolymers.com All Rights Reserved