- HOME
- POLYMER SEARCH
- Thermoplastic
- Polyphenylene Sulfide (PPS)
- Polyphenylene Sulfide (PPS) with 60% Glass Fiber Filler
- Sichuan Deyang Haton® hGR60 Polyphenylene Sulfide, Glass Fiber Reinforced
Sichuan Deyang Haton® hGR60 Polyphenylene Sulfide, Glass Fiber Reinforced
| Category | Polymer , Thermoplastic , Polyphenylene Sulfide (PPS) , Polyphenylene Sulfide (PPS) with 60% Glass Fiber Filler |
| Manufacturer | Sichuan Deyang Chemical Co. Ltd. |
| Trade Name | Haton® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Sichuan Deyang Haton® hGR60 Polyphenylene Sulfide, Glass Fiber Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Injection moldingInformation provided by Sichuan Deyang Chemical Co., LTD
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.80 g/cc | 0.0650 lb/in³ | GB/T 1033.1-2008 |
| Water Absorption | 0.020 % | 0.020 % | GB/T 1034-2008 |
| Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | GB/T 15585-1995 |
| Linear Mold Shrinkage, Transverse | 0.0032 cm/cm | 0.0032 in/in | GB/T 15585-1995 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell L | 115 | 115 | GB/T 3398.2-2008 |
| Tensile Strength | 172 MPa | 24900 psi | GB/T 1040.2-2006 |
| Elongation at Break | 1.0 % | 1.0 % | GB/T1040.2-2006 |
| Flexural Strength | 262 MPa | 38000 psi | GB/T 9341-2008 |
| Flexural Modulus | 19.6 GPa | 2840 ksi | GB/T 9341-2008 |
| Izod Impact, Notched (ISO) | 10.3 kJ/m² | 4.90 ft-lb/in² | GB/T 1843-2008 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 280 °C | 536 °F | GBT/T 19466.3-2004 |
| Deflection Temperature at 1.8 MPa (264 psi) | 270 °C | 518 °F | GB/T 1634.2-2004 |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.60e+16 ohm-cm | 1.60e+16 ohm-cm | GB/T1410-2006 |
| Surface Resistivity per Square | 2.00e+15 ohm | 2.00e+15 ohm | GB/T1410-2006 |
| Dielectric Constant | 4.0 | 4.0 | GB/T 1409-2006 |
| Dielectric Strength | 14.0 kV/mm | 356 kV/in | GB/T1408.1-2006 |
| Dissipation Factor | 0.0010 | 0.0010 | GB/T 1409-2006 |
Users viewing this material also viewed the following:
- Omnia Plastica Omniamid PA6 GHR - HR - at 50% RH
- ICO Polymers ICOFLOâ„¢ 510-5018 400 Micron LDPE Powder
- SABIC Innovative Plastics LNP LUBRILOY D2000 PC (Asia Pacific)
- Zoltek Panex 35® 50k Continuous Tow Commercial Carbon Fiber for Industrial Applications
- Hexcel® HexWeb® HRH-327 - 3/16 - 5.0 Fiberglass Reinforced Polyimide Honeycomb
- Dow Engage® Polyolefin Elastomer
- Abatron AboSeal 8104-15 Polysulfide, Thixotropic or Self-Leveling Sealant and Caulk
- Solvay RHODAPHOSE® TRIS-2 ETHYLEHEXYLPHOSPHITE® Phosphorus Derivative
Copyright © lookpolymers.com All Rights Reserved