PTS Trimid® N6-200N Nylon 6 with Nucleating Agent
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Nucleated |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trimid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trimid® N6-200N Nylon 6 with Nucleating Agent.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.6 % | 1.6 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 79.3 MPa | 11500 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.17 mm |
0.993 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 216 °C | 421 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 64.0 °C | 147 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | <= 216 °C | <= 420 °F | |
| Middle Barrel Temperature | 227 - 254 °C | 440 - 490 °F | |
| Front Barrel Temperature | 238 - 266 °C | 460 - 510 °F | |
| Nozzle Temperature | 238 - 266 °C | 460 - 510 °F | |
| Melt Temperature | 232 - 271 °C | 450 - 520 °F | |
| Mold Temperature | 21.1 - 93.3 °C | 70.0 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Injection Pressure | 82.7 - 172 MPa | 12000 - 25000 psi | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm |
Users viewing this material also viewed the following:
- Plaskolite West Optix® CA - 75 LL General Purpose Acrylic Resin
- Shandong Dongyue Shenzhou New Material Co CHF080 Perfluorosulfonic Acid Ion-Exchange Resin (PFSA)
- SABIC Innovative Plastics LNP THERMOCOMP DX11354 PC (Asia Pacific)
- Teknor Apex Sinvicomp SRF 1703 Polyvinyl Chloride, Rigid
- A. Schulman POLYBATCH™ White B8750A Concentrate Based In HDPE
- Covestro Makrolon® 2856 Polycarbonate
- Adell AL-38 Nylon 66, 40% Glass Reinforced; Mineral Filled
- Barlog Plastics KEBAFORM C 8027 POM Copolymer, 30% mineral reinforced
- Bapolene® 4012F Polypropylene, Compounding/Extrusion Grade
Copyright © lookpolymers.com All Rights Reserved