PTS Trimid® N6-200L Nylon 6 with Lube
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trimid® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trimid® N6-200L Nylon 6 with Lube.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.6 % | 1.6 % | ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 85.5 MPa | 12400 psi | ASTM D638 |
| Elongation at Break | 100 % | 100 % | ASTM D638 |
| Flexural Modulus | 2.83 GPa | 410 ksi | ASTM D790 |
| Izod Impact, Notched | 0.640 J/cm @Thickness 3.17 mm |
1.20 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 216 °C | 421 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 174 °C | 345 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 63.0 °C | 145 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | <= 216 °C | <= 420 °F | |
| Middle Barrel Temperature | 227 - 254 °C | 440 - 490 °F | |
| Front Barrel Temperature | 238 - 266 °C | 460 - 510 °F | |
| Nozzle Temperature | 238 - 266 °C | 460 - 510 °F | |
| Melt Temperature | 232 - 271 °C | 450 - 520 °F | |
| Mold Temperature | 21.1 - 93.3 °C | 70.0 - 200 °F | |
| Drying Temperature | 82.2 °C | 180 °F | |
| Dry Time | 3 - 4 hour | 3 - 4 hour | |
| Injection Pressure | 82.7 - 172 MPa | 12000 - 25000 psi | |
| Back Pressure | 0.000 - 0.345 MPa | 0.000 - 50.0 psi | |
| Screw Speed | 40 - 80 rpm | 40 - 80 rpm |
Users viewing this material also viewed the following:
- Plastcom SLOVAMID 66 GF 15 HI PA66, 15% glass fibre
- Overview of materials for Phenolic, Novolac, Cellulose Filled
- ITW Devcon Metal Repair Stainless Steel Putty (ST), Grey
- Wieland 1916 Wilaform Gold
- A. Schulman PP 1407H-01 Polypropylene High-Impact Polypropylene
- ChevronTexaco HDAX® SAE 30 Ashless Gas Engine Oil
- AK Steel ASTM A 607 Class 2 Formable, Grade 60K Hot Rolled Carbon Steel, Medium/High Strength Low Alloy (HSLA)
- ACC QGel 300 QSI Quantum Silicones High Strength Gel
- BASF Ultramid® A3HG6 HR BK 23591 30% Glass Filled PA66 (Conditioned)
- Chem Polymer Chemlon 214 G Nylon 6, 14% Glass Fiber Reinforced
Copyright © lookpolymers.com All Rights Reserved