Honeywell Capran® Emblem™ 2500M M-Coated Bi-Axially Oriented Nylon Film
| Category | Polymer , Film , Thermoplastic , Nylon |
| Manufacturer | Honeywell |
| Trade Name | Capran® Emblem™ |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Honeywell Capran® Emblem™ 2500M M-Coated Bi-Axially Oriented Nylon Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Capran® Emblem™ 2500M is a bi-axially oriented nylon film. It is a versatile and robust film that satisfies many packaging needs, and has superior resistance to oils, fats, hydrocarbons, and many solvents. It is also microwavable, making it an excellent choice for lidding stock. Capran® Emblem™ 2500M has a polymeric coating that enhances adhesion to a variety of printing inks, coatings, and adhesives. Applications: bag-on-box packaging, packaging for processed meats, cheese, meat snacks, coffee bricks, coffee bags, and pet food, agricultural bags, stand-up shampoo pouches, book covers and metallized balloons. Capran® Emblem™ 2500M is also excellent for metallization processes.Information provided by Honeywell.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.16 g/cc | 0.0420 lb/in³ | Yield Density |
| Water Vapor Transmission | 171 - 202 g/m²/day | 11.0 - 13.0 g/100 in²/day | 100°F / 100%RH); ASTM F1249 |
| Oxygen Transmission Rate | 18.62 - 35.7 cc/m²/day | 1.199 - 2.30 cc/100 in²/day | 77°F / 0% / RH; ASTM D3985 |
| Thickness | 25.4 microns | 1.00 mil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 70 - 110 % | 70 - 110 % | ASTM D882 |
| Film Elongation at Break, TD | 60 - 90 % | 60 - 90 % | ASTM D882 |
| Secant Modulus, MD | 2.41 - 3.55 GPa | 350 - 515 ksi | ASTM D882 |
| Secant Modulus, TD | 2.41 - 3.28 GPa | 350 - 476 ksi | ASTM D882 |
| Coefficient of Friction | 0.21 - 0.41 | 0.21 - 0.41 | film to stainless steel; ASTM D1894 |
| 0.65 - 0.86 | 0.65 - 0.86 | film to film; ASTM D1894 | |
| Tear Strength Test | 1100 - 1500 | 1100 - 1500 | graves tear, grams/mil (initial); ASTM D1004 |
| Elmendorf Tear Strength, MD | 0.591 - 0.748 g/micron | 15.0 - 19.0 g/mil | |
| Film Tensile Strength at Break, MD | 207 - 290 MPa | 30000 - 42000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 221 - 283 MPa | 32000 - 41000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 1.6 - 2.3 % | 1.6 - 2.3 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Shrinkage, TD | 0.20 - 0.70 % | 0.20 - 0.70 % | 320°F / 160°C - 5 minutes; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | <= 3.4 % | <= 3.4 % | ASTM D1003 |
| Gloss | 90 - 140 % | 90 - 140 % | at 20° |
Users viewing this material also viewed the following:
- MV Labs YB400 YbCl3·6H2O Ytterbium chloride hexahydrate
- S&E Specialty Polymers TufTech™ GA-3099LF PVC Compound
- PolyOne Geon™ Vinyl Flexible R343AE Polyvinyl Chloride, Flexible (PVC, Flexible)
- Multibase Multi-Flex® G 7940 TPE Styrene Ethylene Butylene Styrene Block Copolymer
- LATI Latiblend 3675 G/10 ABS/PBT, 10% Glass Fiber Reinforced
- SABIC Innovative Plastics LNP LUBRICOMP PFI12R PA 6
- Saint-Gobain Chemlam® RL® RL4000 PTFE-Coated Non-woven Aramid Reinforced Laminate
- Chase Plastics CP Pryme® NNA100 (Dry) ABS Polyamide Alloy
- LNP Thermocomp® JF-1006 E LE BK8-055 Polyethersulfone, Glass Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved