- PTS Trilac® ABS-HH2500 Super High Heat ABS Resin
PTS Trilac® ABS-HH2500 Super High Heat ABS Resin
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Heat Resistant, Molded |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Trilac® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Trilac® ABS-HH2500 Super High Heat ABS Resin.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ASTM D792 |
| Melt Flow | 0.20 g/10 min @Load 3.80 kg, Temperature 230 °C |
0.20 g/10 min @Load 8.38 lb, Temperature 446 °F |
|
| 1.8 g/10 min @Load 10.0 kg, Temperature 220 °C |
1.8 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Yield | 44.0 MPa | 6380 psi | ASTM D638 |
| Flexural Yield Strength | 63.4 MPa | 9200 psi | ASTM D790 |
| Flexural Modulus | 2.07 GPa | 300 ksi | ASTM D790 |
| Izod Impact, Notched | 1.39 J/cm @Thickness 6.35 mm |
2.60 ft-lb/in @Thickness 0.250 in |
ASTM D256 |
| 2.14 J/cm @Thickness 3.17 mm |
4.01 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 122 °C | 252 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 113 °C | 235 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 193 °C | 380 °F | |
| Middle Barrel Temperature | 216 °C | 420 °F | |
| Front Barrel Temperature | 232 °C | 450 °F | |
| Melt Temperature | 246 - 260 °C | 475 - 500 °F | Nozzle temp not greater than stock |
| Mold Temperature | 48.9 - 65.6 °C | 120 - 150 °F | |
| Drying Temperature | 87.8 - 93.3 °C | 190 - 200 °F | |
| Dry Time | 2 - 24 hour | 2 - 24 hour | |
| Injection Pressure | 68.9 - 82.7 MPa | 10000 - 12000 psi | |
| Back Pressure | 0.689 MPa | 100 psi | |
| Screw Speed | 50 - 60 rpm | 50 - 60 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Injection Fill Speed | Slow to Moderate |
Users viewing this material also viewed the following:
- Mytex Polymers AS33L(W)-06 Polypropylene, Rubber modified, Talc filled, Compounded
- Oceanchem Group Zinc Bromide
- SABIC Innovative Plastics Lexan® EXL1444 PC Copolymer
- Karina E TR-600N35/1-YT-A Ivory TR (SP31503)
- ICO Polymers ICOFLOâ„¢ 510-5062 500 Micron LDPE Powder
- Saint-Gobain COHRlastic® 3016 Low Temperature Flexibility Silicone Coated Fabric
- Sumitomo Bakelite North America RX® 630 Fiberglass Reinforced Phenolic
- Borealis Borstar® MB7542 High Density Polyethylene for Injection Molding
- Epoxy Technology EPO-TEK® 360 Low Viscosity Optical Epoxy Adhesive
Copyright © lookpolymers.com All Rights Reserved