Polimeri Europa Riblene® FF 22 Low Density Polyethylene - Blown Film Extrusion

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE , Low Density Polyethylene (LDPE), Film Grade
Manufacturer Polimeri Europa (Former EniChem)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Polimeri Europa Riblene® FF 22 Low Density Polyethylene - Blown Film Extrusion.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Riblene FF 22 is a high molecular weight low density polyethylene (LDPE), with added slip agent, suitable for blown film extrusion. Riblene FF 22 is characterized by a good melt strength leading to a good bubble stability during extrusion.Films manufactured with Riblene FF 22 are easily heat shrinkable and characterized by good mechanical properties.Main Applications: Riblene FF 22 is recommended for the production of shrink film for medium loads, industrial bags, carrier bags and blend.Information provided by Polimeri Europa.
Physical Properties Metric English Comments
Specific Gravity 0.921 g/cc
0.921 g/cc
ISO 1183
Thickness 40.0 - 150 microns
1.57 - 5.91 mil
Recommended
Melt Flow 0.80 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.80 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ISO 1133
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.0 MPa
1450 psi
ISO 527-3
Film Tensile Strength at Yield, TD 10.0 MPa
1450 psi
ISO 527-3
Film Elongation at Break, MD 400 %
400 %
ISO 527-3
Film Elongation at Break, TD 600 %
600 %
ISO 527-3
Coefficient of Friction, Dynamic 0.13
0.13
ISO 8295
Elmendorf Tear Strength, MD 3.057 g/micron
77.65 g/mil
ISO 6383-2
Elmendorf Tear Strength, TD 4.076 g/micron
103.5 g/mil
ISO 6383-2
Dart Drop Test 280 g
0.617 lb
F50; ISO 7765-1
Film Tensile Strength at Break, MD 25.0 MPa
3630 psi
ISO 527-3
Film Tensile Strength at Break, TD 22.0 MPa
3190 psi
ISO 527-3
1% Secant Modulus, MD 165 MPa
23900 psi
ISO 527-3
1% Secant Modulus, TD 185 MPa
26800 psi
ISO 527-3
Thermal Properties Metric English Comments
Melting Point 112 °C
234 °F
Internal method
Vicat Softening Point 91.0 °C

@Load 1.00 kg
196 °F

@Load 2.20 lb
ISO 306/A
Brittleness Temperature <= -75.0 °C
<= -103 °F
ASTM D746
Optical Properties Metric English Comments
Haze 8.5 %
8.5 %
ISO 14782
Gloss 60 %
60 %
45°; ASTM D2457