PTS POM-270 27.0 MFI Acetal Copolymer
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Unreinforced |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS POM-270 27.0 MFI Acetal Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | ASTM D792 |
| Water Absorption | 0.22 % | 0.22 % | ASTM D570 |
| Melt Flow | 27 g/10 min @Load 10.0 kg, Temperature 220 °C |
27 g/10 min @Load 22.0 lb, Temperature 428 °F |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell M | 80 | 80 | ASTM D785 |
| Tensile Strength, Yield | 59.3 MPa | 8600 psi | ASTM D638 |
| Elongation at Break | 38 % | 38 % | ASTM D638 |
| Flexural Yield Strength | 85.5 MPa | 12400 psi | ASTM D790 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790 |
| Izod Impact, Notched | 0.430 J/cm @Thickness 3.17 mm |
0.806 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 158 °C | 316 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 110 °C | 230 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 160 - 180 °C | 320 - 356 °F | |
| Middle Barrel Temperature | 180 - 200 °C | 356 - 392 °F | |
| Front Barrel Temperature | 190 - 215 °C | 374 - 419 °F | |
| Nozzle Temperature | 190 - 215 °C | 374 - 419 °F | |
| Melt Temperature | 200 - 225 °C | 392 - 437 °F | |
| Mold Temperature | 60.0 - 100 °C | 140 - 212 °F | |
| Drying Temperature | 90.0 - 110 °C | 194 - 230 °F | |
| Dry Time | 3 - 6 hour | 3 - 6 hour | |
| Screw Speed | 50 - 100 rpm | 50 - 100 rpm |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Processing Purging Material | Polyethylene/Polystyrene |
Users viewing this material also viewed the following:
- Renegade Materials Corporation MVK-14 Polyimide FreeForm™ S2-Glass Fabric
- Total Finathene® 56020 HDPE, blow molding, sheet (discontinued **)
- A. Schulman SCHULADUR® B GF25LB 25% Glass Fiber Reinforced, Lubricated PET
- Covestro Apec® HT KU 1-9354 High-Heat Polycarbonate
- Colorite Polymers 1104 Clear Extrusion Vinyl Compound
- Aaron Industries AAROPRENE® ATPR 1000 50A Elastomeric Compound
- Arlon 51224R015P 0.015" Semi-cured Silicone Rubber with Fiberglass Substrate
- Styrolution Luran® 368 R Crystal Clear Transparent 77851 SAN
- SABIC Innovative Plastics LNP VERTON PX00700 PA 6 (Asia Pacific)
Copyright © lookpolymers.com All Rights Reserved