PTS PCA-1010HF High Flow Polycarbonate/ABS Alloy

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Polymer Technology & Services, LLC (PTS)
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF PTS PCA-1010HF High Flow Polycarbonate/ABS Alloy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
Physical Properties Metric English Comments
Density 1.15 g/cc
0.0415 lb/in³
ASTM D792
Water Absorption 0.10 %
0.10 %
24 hours at 73°F; ASTM D570
Mechanical Properties Metric English Comments
Tensile Strength, Yield 55.2 MPa

@Thickness 3.17 mm
 8010 psi

@Thickness 0.125 in
 ASTM D638
Elongation at Break 125 %

@Thickness 3.17 mm
 125 %

@Thickness 0.125 in
 ASTM D638
Flexural Yield Strength 82.7 MPa

@Thickness 3.17 mm
 12000 psi

@Thickness 0.125 in
 ASTM D790
Flexural Modulus 2.21 GPa

@Thickness 3.17 mm
 321 ksi

@Thickness 0.125 in
 ASTM D790
Izod Impact, Notched 5.34 J/cm

@Thickness 3.17 mm
 10.0 ft-lb/in

@Thickness 0.125 in
 ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 107 °C
225 °F
ASTM D648
Processing Properties Metric English Comments
Rear Barrel Temperature 221 - 229 °C
430 - 445 °F
Middle Barrel Temperature 224 - 235 °C
435 - 455 °F
Front Barrel Temperature 229 - 241 °C
445 - 465 °F
Nozzle Temperature 232 - 243 °C
450 - 470 °F
Melt Temperature 238 - 254 °C
460 - 490 °F
Mold Temperature 68.3 - 87.8 °C
155 - 190 °F
Drying Temperature 104 °C
220 °F
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 68.9 - 138 MPa
10000 - 20000 psi
Back Pressure 0.345 - 0.689 MPa
50.0 - 100 psi
Shot Size 50 - 80 %
50 - 80 %
Screw Speed 40 - 70 rpm
40 - 70 rpm