Arlon 51426W015 0.015" Cured/Uncured Silicone Rubber with Fiberglass Substrate

Category	Polymer , Thermoset , Silicone , Silicone, Molded, Glass Fiber Filled
Manufacturer	Arlon
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Arlon 51426W015 0.015" Cured/Uncured Silicone Rubber with Fiberglass Substrate.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Design/Construction:Side 1: Cured Silicone RubberSubstrate: Prime Coated 7628 FiberglassSide 2: Uncured Silicone RubberInterleave: 3 mil PolyethyleneThis data represents typical values for the production material and should not be used as material specifications.Information provided by ARLON Silicone Technologies Division.

Physical Properties	Metric	English	Comments
Thickness	76.2 microns	3.00 mil	Side 1
	102 microns	4.00 mil	Side 2
	203 microns	8.00 mil	Substrate
	381 microns	15.0 mil	Overall Thickness

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	58	58	Silicone Property
Tensile Strength	6.21 MPa	900 psi	Silicone Property
Elongation at Break	350 %	350 %	Silicone Property
Peel Strength	>= 1.05 kN/m	>= 6.00 pli	Bond Strength, side 2 to side 2

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Inert	232 °C	450 °F
Minimum Service Temperature, Air	-56.7 °C	-70.0 °F
Flammability Test	3.0	3.0	Inches; Char Length; FTMS 191A; Method 5903
	25	25	Seconds; Flame and Glow Time; FTMS 191A; Method 5903

Electrical Properties	Metric	English	Comments
Dielectric Strength	>= 15.7 kV/mm	>= 400 kV/in

Processing Properties	Metric	English	Comments
Cure Time	120 min @Temperature 204 °C	2.00 hour @Temperature 400 °F	Recommended Post Cure Cycle
	15.0 min @Pressure 0.345 MPa, Temperature 177 °C	0.250 hour @Pressure 50.0 psi, Temperature 350 °F	Recommended Cure Cycle
Shelf Life	6.00 Month @Temperature 23.9 °C	6.00 Month @Temperature 75.0 °F

Descriptive Properties	Value	Comments
Color	White
Total Product Weight (oz/yd2)	16.8
Uncoated Fabric Break Strength (lb/in)	200	Fill direction
	250	Warp direction