Overview of materials for Nylon 66, Glass/Carbon Fiber Filled

Category Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Glass/Carbon Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Nylon 66, Glass/Carbon Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Nylon 66, Glass/Carbon Fiber Filled". Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.21 - 1.54 g/cc
0.0437 - 0.0556 lb/in³
Average value: 1.35 g/cc Grade Count:20
Filler Content 50.0 %
50.0 %
Average value: 50.0 % Grade Count:3
Water Absorption 0.200 - 1.80 %
0.200 - 1.80 %
Average value: 0.967 % Grade Count:12
Linear Mold Shrinkage 0.00100 - 0.00600 cm/cm
0.00100 - 0.00600 in/in
Average value: 0.00332 cm/cm Grade Count:17
Mechanical Properties Metric English Comments
Hardness, Rockwell R 115 - 120
115 - 120
Average value: 118 Grade Count:4
Tensile Strength, Ultimate 138 - 294 MPa
20000 - 42600 psi
Average value: 208 MPa Grade Count:17
Tensile Strength, Yield 131 - 165 MPa
19000 - 24000 psi
Average value: 149 MPa Grade Count:4
Elongation at Break 1.00 - 5.00 %
1.00 - 5.00 %
Average value: 2.77 % Grade Count:10
Elongation at Yield 2.00 - 3.90 %
2.00 - 3.90 %
Average value: 2.78 % Grade Count:10
Modulus of Elasticity 6.90 - 26.9 GPa
1000 - 3900 ksi
Average value: 15.3 GPa Grade Count:15
Flexural Yield Strength 179 - 432 MPa
26000 - 62700 psi
Average value: 295 MPa Grade Count:18
Flexural Modulus 6.89 - 21.4 GPa
1000 - 3100 ksi
Average value: 12.0 GPa Grade Count:20
Izod Impact, Notched 0.530 - 3.20 J/cm
0.993 - 5.99 ft-lb/in
Average value: 1.39 J/cm Grade Count:12
Izod Impact, Unnotched 4.59 - 10.0 J/cm
8.60 - 18.8 ft-lb/in
Average value: 7.76 J/cm Grade Count:5
Charpy Impact Unnotched 4.00 - 6.50 J/cm²
19.0 - 30.9 ft-lb/in²
Average value: 5.23 J/cm² Grade Count:10
5.00 - 5.00 J/cm²

@Temperature -30.0 - -30.0 °C
23.8 - 23.8 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 5.00 J/cm² Grade Count:1
Charpy Impact, Notched 1.00 - 1.20 J/cm²
4.76 - 5.71 ft-lb/in²
Average value: 1.07 J/cm² Grade Count:7
1.00 - 1.00 J/cm²

@Temperature -30.0 - -30.0 °C
4.76 - 4.76 ft-lb/in²

@Temperature -22.0 - -22.0 °F
Average value: 1.00 J/cm² Grade Count:1
Coefficient of Friction 0.200 - 0.320
0.200 - 0.320
Average value: 0.287 Grade Count:4
Coefficient of Friction, Static 0.170 - 0.280
0.170 - 0.280
Average value: 0.250 Grade Count:4
Thermal Properties Metric English Comments
CTE, linear 19.8 - 30.0 µm/m-°C
11.0 - 16.7 µin/in-°F
Average value: 22.5 µm/m-°C Grade Count:5
Thermal Conductivity 0.280 - 0.400 W/m-K
1.94 - 2.78 BTU-in/hr-ft²-°F
Average value: 0.360 W/m-K Grade Count:3
Melting Point 249 - 275 °C
480 - 527 °F
Average value: 261 °C Grade Count:3
Maximum Service Temperature, Air 120 - 160 °C
248 - 320 °F
Average value: 140 °C Grade Count:9
Deflection Temperature at 0.46 MPa (66 psi) 230 - 256 °C
446 - 493 °F
Average value: 250 °C Grade Count:6
Deflection Temperature at 1.8 MPa (264 psi) 220 - 257 °C
428 - 495 °F
Average value: 245 °C Grade Count:15
Flammability, UL94 HB
HB
Grade Count:6
Electrical Properties Metric English Comments
Surface Resistance 10.0 - 1.00e+8 ohm
10.0 - 1.00e+8 ohm
Average value: 1.00e+7 ohm Grade Count:13
Insulation Resistance 100 - 1.00e+8 ohm
100 - 1.00e+8 ohm
Average value: 1.11e+7 ohm Grade Count:9
Processing Properties Metric English Comments
Processing Temperature 290 °C
554 °F
Average value: 290 °C Grade Count:11
Nozzle Temperature 280 - 300 °C
536 - 572 °F
Average value: 290 °C Grade Count:9
Melt Temperature 260 - 310 °C
500 - 590 °F
Average value: 298 °C Grade Count:14
Mold Temperature 66.0 - 121 °C
151 - 250 °F
Average value: 100 °C Grade Count:14
Drying Temperature 75.0 - 107 °C
167 - 225 °F
Average value: 90.1 °C Grade Count:12