Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Overview of materials for Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
This property data is a summary of similar materials in the MatWeb database for the category "Acrylonitrile Butadiene Styrene (ABS), 30% Glass Fiber Filled". Specific grades with glass content between 25% and 34% are included. Each property range of values reported is minimum and maximum values of appropriate MatWeb entries. The comments report the average value, and number of data points used to calculate the average. The values are not necessarily typical of any specific grade, especially less common values and those that can be most affected by additives or processing methods.
Physical Properties Metric English Comments
Density 1.17 - 1.50 g/cc
0.0423 - 0.0542 lb/in³
Average value: 1.28 g/cc Grade Count:46
Filler Content 25.0 - 33.0 %
25.0 - 33.0 %
Average value: 29.3 % Grade Count:10
Water Absorption 0.120 - 0.300 %
0.120 - 0.300 %
Average value: 0.142 % Grade Count:12
Maximum Moisture Content 0.0200 - 0.150
0.0200 - 0.150
Average value: 0.0633 Grade Count:3
Linear Mold Shrinkage 0.00100 - 0.00900 cm/cm
0.00100 - 0.00900 in/in
Average value: 0.00177 cm/cm Grade Count:44
Melt Flow 0.100 - 10.0 g/10 min
0.100 - 10.0 g/10 min
Average value: 3.44 g/10 min Grade Count:20
Ash 25.0 - 31.0 %
25.0 - 31.0 %
Average value: 29.3 % Grade Count:6
Mechanical Properties Metric English Comments
Hardness, Rockwell R 88.0 - 115
88.0 - 115
Average value: 108 Grade Count:21
Tensile Strength, Ultimate 53.8 - 103 MPa
7800 - 15000 psi
Average value: 83.6 MPa Grade Count:25
Tensile Strength, Yield 51.7 - 117 MPa
7500 - 17000 psi
Average value: 85.9 MPa Grade Count:32
Elongation at Break 1.00 - 6.00 %
1.00 - 6.00 %
Average value: 2.61 % Grade Count:34
Elongation at Yield 1.00 - 6.00 %
1.00 - 6.00 %
Average value: 2.88 % Grade Count:10
Modulus of Elasticity 4.30 - 10.0 GPa
624 - 1450 ksi
Average value: 6.97 GPa Grade Count:18
Flexural Yield Strength 12.8 - 162 MPa
1850 - 23500 psi
Average value: 119 MPa Grade Count:40
Flexural Modulus 4.14 - 10.0 GPa
600 - 1450 ksi
Average value: 7.29 GPa Grade Count:44
Izod Impact, Notched 0.402 - 1.23 J/cm
0.753 - 2.30 ft-lb/in
Average value: 0.681 J/cm Grade Count:45
0.600 - 0.600 J/cm

@Temperature 0.000 - 0.000 °C
1.12 - 1.12 ft-lb/in

@Temperature 32.0 - 32.0 °F
Average value: 0.600 J/cm Grade Count:1
Izod Impact, Unnotched 2.14 - 4.81 J/cm
4.00 - 9.00 ft-lb/in
Average value: 3.28 J/cm Grade Count:18
Izod Impact, Notched (ISO) 4.60 - 6.00 kJ/m²
2.19 - 2.86 ft-lb/in²
Average value: 5.53 kJ/m² Grade Count:3
Thermal Properties Metric English Comments
CTE, linear 17.0 - 30.6 µm/m-°C
9.44 - 17.0 µin/in-°F
Average value: 27.9 µm/m-°C Grade Count:11
Deflection Temperature at 0.46 MPa (66 psi) 98.9 - 200 °C
210 - 392 °F
Average value: 112 °C Grade Count:27
Deflection Temperature at 1.8 MPa (264 psi) 91.1 - 180 °C
196 - 356 °F
Average value: 104 °C Grade Count:39
Vicat Softening Point 103 - 115 °C
217 - 239 °F
Average value: 109 °C Grade Count:8
Flammability, UL94 HB - V-0
HB - V-0
Grade Count:20
Electrical Properties Metric English Comments
Electrical Resistivity 1.00e+9 - 1.00e+16 ohm-cm
1.00e+9 - 1.00e+16 ohm-cm
Average value: 6.46e+15 ohm-cm Grade Count:13
Dielectric Strength 15.7 - 26.0 kV/mm
400 - 660 kV/in
Average value: 18.5 kV/mm Grade Count:10
Arc Resistance 60.0 - 120 sec
60.0 - 120 sec
Average value: 81.7 sec Grade Count:3
Processing Properties Metric English Comments
Processing Temperature 193 - 232 °C
380 - 450 °F
Average value: 215 °C Grade Count:4
Nozzle Temperature 200 - 274 °C
392 - 525 °F
Average value: 230 °C Grade Count:7
Melt Temperature 160 - 288 °C
320 - 550 °F
Average value: 221 °C Grade Count:15
Mold Temperature 40.0 - 93.3 °C
104 - 200 °F
Average value: 67.8 °C Grade Count:18
Drying Temperature 79.4 - 100 °C
175 - 212 °F
Average value: 84.9 °C Grade Count:11
Moisture Content 0.0100 - 0.100 %
0.0100 - 0.100 %
Average value: 0.0850 % Grade Count:6
Dew Point -17.8 °C
0.000 °F
Average value: -17.8 °C Grade Count:3
Injection Pressure 4.83 - 103 MPa
700 - 15000 psi
Average value: 53.6 MPa Grade Count:11