- Nilit RECONYL B KV30 Recycled nylon 6 for injection molding, 30% glass ball reinforced
Nilit RECONYL B KV30 Recycled nylon 6 for injection molding, 30% glass ball reinforced
| Category | Polymer , Renewable/Recycled Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit RECONYL B KV30 Recycled nylon 6 for injection molding, 30% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Recycled nylon 6 for injection molding (available only in black).Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in³ | ISO 1183 |
| Water Absorption | 1.5 - 2.5 % | 1.5 - 2.5 % | ISO 62 |
| Water Absorption at Saturation | 6.0 - 7.0 % | 6.0 - 7.0 % | ISO 62 |
| Linear Mold Shrinkage | 0.0090 - 0.017 cm/cm | 0.0090 - 0.017 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 165 MPa | 23900 psi | ISO 2039-1 |
| Tensile Strength at Break | 75.0 MPa | 10900 psi | ISO 527 |
| Elongation at Break | 6.0 % | 6.0 % | ISO 527 |
| Tensile Modulus | 4.00 GPa | 580 ksi | ISO 527 |
| Flexural Strength | 95.0 MPa | 13800 psi | ISO 178 |
| Flexural Modulus | 3.40 GPa | 493 ksi | ISO 178 |
| Charpy Impact Unnotched | 3.60 J/cm² | 17.1 ft-lb/in² | DIN 53453 |
| 2.70 J/cm² @Temperature -40.0 °C |
12.8 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 98.0 °C | 208 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 180 °C | 356 °F | ISO 75 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N1013THL Nylon 6/6 (Cond)
- Solvay Specialty Polymers Udel® P-3703 Polysulfone (PSU) (Unverified Data**)
- Lehmann & Voss LUVOCOM® AC-80/TF/22/BK Polyacetal-copolymer, with PTFE
- Multibase Multi-Flamâ„¢ 2318 PP Polypropylene
- SABIC Innovative Plastics LNP LUBRICOMP RA004 PA 66
- SABIC Innovative Plastics LNP THERMOCOMP MF002S PP
- Total PSI 4440(EU) High Impact Polystyrene
- Diamond Polymers DIAMALOY ABSPC 750 HF ABS/PC Alloy, Non-Halogen, Flame Retardant
- Fainplast Compounds GS 6612 Flexible PVC, Injection Molding for Footwear
- Arlon 48101R008 0.008" (0.203 mm) Uncured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved