SABIC Innovative Plastics LNP VERTON UX06451 PPA (Asia Pacific)
| Category | Polymer , Thermoplastic , Polyphthalamide (PPA) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | LNP VERTON |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics LNP VERTON UX06451 PPA (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
LNP* Verton* UX06451 is a compound based on Polyphthalamide resin containing Long Glass Fiber.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.63 g/cc | 0.0589 lb/in³ | ISO 1183 |
| 1.63 g/cc | 0.0589 lb/in³ | ASTM D792 | |
| Moisture Absorption | 0.300 % | 0.300 % | 50% RH, 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.00060 cm/cm @Time 86400 sec |
0.00060 in/in @Time 24.0 hour |
ISO 294 |
| Linear Mold Shrinkage, Transverse | 0.0020 cm/cm @Time 86400 sec |
0.0020 in/in @Time 24.0 hour |
ISO 294 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 274 MPa | 39700 psi | ASTM D638 |
| 275 MPa | 39900 psi | ISO 527 | |
| Elongation at Break | 1.7 % | 1.7 % | ISO 527 |
| 1.9 % | 1.9 % | ASTM D638 | |
| Tensile Modulus | 19.0 GPa | 2760 ksi | 1 mm/min; ISO 527 |
| 19.3 GPa | 2800 ksi | 50 mm/min; ASTM D638 | |
| Flexural Strength | 375 MPa | 54400 psi | ISO 178 |
| Flexural Modulus | 17.4 GPa | 2520 ksi | ISO 178 |
| Izod Impact, Notched | 4.11 J/cm | 7.70 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 14.95 J/cm | 28.01 ft-lb/in | ASTM D4812 |
| Izod Impact, Notched (ISO) | 40.0 kJ/m² | 19.0 ft-lb/in² | 80*10*4; ISO 180/1A |
| Izod Impact, Unnotched (ISO) | 75.0 kJ/m² | 35.7 ft-lb/in² | 80*10*4; ISO 180/1U |
| Impact Test | 14.0 J | 10.3 ft-lb | Multiaxial Impact; ISO 6603 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 22.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
12.2 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
| CTE, linear, Transverse to Flow | 32.0 µm/m-°C @Temperature -40.0 - 40.0 °C |
17.8 µin/in-°F @Temperature -40.0 - 104 °F |
ISO 11359-2 |
Users viewing this material also viewed the following:
- Resinlab® EP1121-4 Adhesive / Casting Resin
- Hong Kun Group 2,4,6-Trichloropyrimidine Pharmaceutical Intermediate
- Haynes 556® alloy, 30% cold reduction, 1010°C anneal for 5 minutes
- Tipco Tipcolite® TG 211 Phenolic Compound, Mineral & Wood Flour, Soft Flow & High Electrical Properties
- EMS-Grivory Grivory® TR 90 PAMACM12
- DuPont Teijin Films Melinex® 437 Polyester Film, 200 Gauge
- Alliance N-35SH Neodymium Iron Boron Magnetic Material
- 3M 9731 Double Coated Tape
- LNP Thermotuf® QF-1006 HI Polyamide 6/10 Copolymer, Glass Fiber Reinforcement (discontinued **)
Copyright © lookpolymers.com All Rights Reserved