- Nilit Polynil® P50 Standard Viscosity Nylon 66
Nilit Polynil® P50 Standard Viscosity Nylon 66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Unreinforced |
| Manufacturer | Nilit |
| Trade Name | Polynil® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit Polynil® P50 Standard Viscosity Nylon 66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Standard viscosityApplication: CompoundingInformation provided by NILIT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.5 % | 1.5 % | 24h in H<sub>2</sub>O; sim. ISO 62 |
| Water Absorption at Saturation | 8.5 % | 8.5 % | sim. ISO 62 |
| Viscosity Measurement | 50 | 50 | relative viscosity (formic acid); ASTM D789 |
| Linear Mold Shrinkage, Flow | 0.013 cm/cm | 0.013 in/in | Nilit |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 81.01 MPa | 11750 psi | ASTM D638 |
| Elongation at Break | >= 40 % | >= 40 % | ASTM D638 |
| Elongation at Yield | 6.0 % | 6.0 % | ASTM D638 |
| Tensile Modulus | 3.03 GPa | 440 ksi | ASTM D638 |
| Flexural Strength | 120 MPa | 17400 psi | ASTM D790 |
| Flexural Modulus | 2.85 GPa | 413 ksi | ASTM D790 |
| Izod Impact, Notched (ISO) | 5.46 kJ/m² | 2.60 ft-lb/in² | ASTM D256 |
| 4.41 kJ/m² @Temperature -30.0 °C |
2.10 ft-lb/in² @Temperature -22.0 °F |
ASTM D256 | |
| Charpy Impact Unnotched | NB | NB | ISO 179 |
| Charpy Impact, Notched | 0.600 J/cm² | 2.86 ft-lb/in² | ISO 179 |
| 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 225 °C | 437 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 85.0 °C | 185 °F | ASTM D648 |
| Vicat Softening Point | 240 °C | 464 °F | 49 N; ASTM D1525 |
| 255 °C | 491 °F | 9.8 N; ASTM D1525 | |
| Flammability, UL94 | V-2 @Thickness 0.800 mm |
V-2 @Thickness 0.0315 in |
|
| V-2 @Thickness 1.60 mm |
V-2 @Thickness 0.0630 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Comparative Tracking Index | >= 600 V | >= 600 V | UL 746 |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics LNP COLORCOMP AX03654 ABS
- SABIC Innovative Plastics LNP FARADEX MS002 PP (Europe-Africa-Middle East)
- Lehmann & Voss LUVOCOM® 1106-8087/BL Polyether imide, unreinforced, laser markable
- Solvay Specialty Polymers Radel® R-5500 Polyphenylsulfone (PPSU)
- Teknor Apex APEX® RE 8003 Polyvinyl Chloride, Rigid
- Solvay TECHNYL® A 216 V20 PA66, 20% glass fiber, Conditioned
- A. Schulman POLYBATCH™ Gold 7060E POLYBATCH® Concentrate Based In LDPE
- Covestro Bayfit® High Density Polyurethane Flexible Molded Foam, High Density
Copyright © lookpolymers.com All Rights Reserved