SABIC Innovative Plastics Lexan® SFX173RU PC (Asia Pacific)
| Category | Polymer , Thermoplastic , Polycarbonate (PC) |
| Manufacturer | SABIC Innovative Plastics (GE Plastics) |
| Trade Name | Lexan® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | SABIC Innovative Plastics Lexan® SFX173RU PC (Asia Pacific).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
SFX173RU is a transparent SecurFX grade with high flow, mold release and UV stabilizer. This grade is for security applications and contains proprietary authentication technology.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.20 g/cc | 1.20 g/cc | ASTM D792 |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm @Thickness 3.20 mm |
0.0050 - 0.0070 in/in @Thickness 0.126 in |
SABIC Method |
| Melt Flow | 25 g/10 min @Load 1.20 kg, Temperature 300 °C |
25 g/10 min @Load 2.65 lb, Temperature 572 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 65.0 MPa | 9430 psi | Type I, 50 mm/min; ASTM D638 |
| Tensile Strength, Yield | 62.0 MPa | 8990 psi | Type I, 50 mm/min; ASTM D638 |
| Elongation at Break | 120 % | 120 % | Type I, 50 mm/min; ASTM D638 |
| Elongation at Yield | 8.0 % | 8.0 % | Type I, 50 mm/min; ASTM D638 |
| Tensile Modulus | 1.57 GPa | 228 ksi | 50 mm/min; ASTM D638 |
| Flexural Yield Strength | 93.0 MPa | 13500 psi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Flexural Modulus | 2.30 GPa | 334 ksi | 1.3 mm/min, 50 mm span; ASTM D790 |
| Izod Impact, Notched | 6.40 J/cm | 12.0 ft-lb/in | ASTM D256 |
| Dart Drop, Total Energy | 58.0 J @Temperature 23.0 °C |
42.8 ft-lb @Temperature 73.4 °F |
ASTM D3763 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 126 °C @Thickness 3.20 mm |
259 °F @Thickness 0.126 in |
unannealed; ASTM D648 |
| Vicat Softening Point | 144 °C | 291 °F | Rate B/50; ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | transparent; thickness not quantified |
Users viewing this material also viewed the following:
- DuPont Performance Polymers Hypalon® 20 Chlorosulfonated Polyethylene Rubber, Peroxide Cured Carbon Black Filled Compound
- Iran Petrochemical (PCC) PET BG-841 Polyethylene Terephthalate
- LATI Latilon 28D-V0 PC, Flame Retardant
- Zoltek Pyron® Oxidized Pan Staple Fiber
- CIMBAR CIMTUFF® 9107 Talc
- AK Steel 439 Ferritic Stainless steel
- BASF Ultramid® B3GM35 BK 60564 40% Glass/Mineral Filled PA6 (Conditioned)
- TSE Industries Millathane® CM Millable Polyether Urethane Rubber with 75 PHR N650 Filler
- DuPont Performance Polymers Neoprene AD-5 Polychloroprene Rubber (discontinued **)
Copyright © lookpolymers.com All Rights Reserved