Nilit Nilamid A G5 FR PH1 25% Glass Fiber Reinforced, Flame Retardant PA66
| Category | Polymer , Thermoplastic , Nylon , Nylon 66 , Nylon 66, 30% Glass Fiber Filled |
| Manufacturer | Nilit |
| Trade Name | Nilamid |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit Nilamid A G5 FR PH1 25% Glass Fiber Reinforced, Flame Retardant PA66.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Nilamid A G5 FR PH1 combines flame retardancy with outstanding mechanical performance. This product has a complete yellow card, with RTI and CTI listings. The formulation has been optimized for low phosphate release, to limit the formation of deposits on electrical contacts. The material has a red-brownish natural color.Key characteristics: UL 94 V0 at 1.5 mmHigh strength and stiffnessRTI listing up to 110°C at 0.4 mmHigh CTI: 600VLow phosphate releaseInformation provided by NILIT.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.38 g/cc | 0.0499 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 0.80 % | 0.80 % | 23°C, 24h in H<sub>2</sub>O; sim. ISO 62 |
| Water Absorption at Saturation | 5.5 % | 5.5 % | sim. ISO 62 |
| Linear Mold Shrinkage, Flow | 0.0060 cm/cm | 0.0060 in/in | Euronil |
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | Euronil |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 150 MPa | 21800 psi | ISO 527, ASTM D638 |
| Elongation at Break | 2.5 % | 2.5 % | |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527, ASTM D638 |
| Flexural Yield Strength | 210 MPa | 30500 psi | ISO 178, ASTM D790 |
| 125 MPa @Temperature 90.0 °C |
18100 psi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Flexural Modulus | 8.20 GPa | 1190 ksi | ISO 178, ASTM D790 |
| 4.30 GPa @Temperature 90.0 °C |
624 ksi @Temperature 194 °F |
ISO 178, ASTM D790 | |
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -30.0 °C |
3.33 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A |
| 8.50 kJ/m² @Temperature 23.0 °C |
4.04 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A | |
| Charpy Impact Unnotched | 3.80 J/cm² | 18.1 ft-lb/in² | ISO 179 |
| 2.70 J/cm² @Temperature -30.0 °C |
12.8 ft-lb/in² @Temperature -22.0 °F |
ISO 179 | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | ISO 179 |
| 0.500 J/cm² @Temperature -30.0 °C |
2.38 ft-lb/in² @Temperature -22.0 °F |
ISO 179 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 120 °C | 248 °F | 20,000 hr; IEC 216 |
| Deflection Temperature at 0.46 MPa (66 psi) | 250 °C | 482 °F | ISO 75, ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 245 °C | 473 °F | ISO 75, ASTM D648 |
| Vicat Softening Point | 250 °C | 482 °F | 49 N; ISO 306, ASTM D1525 |
| 255 °C | 491 °F | 9.8 N; ISO 306, ASTM D1525 | |
| Flammability, UL94 | V-0 @Thickness 0.800 mm |
V-0 @Thickness 0.0315 in |
|
| V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
||
| V-0 @Thickness 3.20 mm |
V-0 @Thickness 0.126 in |
||
| Oxygen Index | 29 % | 29 % | ASTM D2863 |
| Glow Wire Test | 960 °C @Thickness 3.20 mm |
1760 °F @Thickness 0.126 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| 960 °C @Thickness 0.800 mm |
1760 °F @Thickness 0.0315 in |
Glow Wire Flammability Index; IEC 694-2-12 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Dielectric Strength | 20.0 kV/mm @Thickness 2.00 mm |
508 kV/in @Thickness 0.0787 in |
ASTM D149 |
| Comparative Tracking Index | 500 V @Thickness 3.20 mm |
500 V @Thickness 0.126 in |
Sol. A; IEC 112, UL 746A |
| 500 V @Thickness 3.20 mm |
500 V @Thickness 0.126 in |
Sol. B; IEC 112, UL 746A |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Nozzle Temperature | 275 - 285 °C | 527 - 545 °F | |
| Zone 1 | 260 - 280 °C | 500 - 536 °F | hopper |
| Zone 2 | 260 - 280 °C | 500 - 536 °F | |
| Zone 3 | 270 - 280 °C | 518 - 536 °F | |
| Zone 4 | 275 - 285 °C | 527 - 545 °F | |
| Melt Temperature | 275 - 290 °C | 527 - 554 °F | Do not melt above 290°C |
| Mold Temperature | 90.0 - 110 °C | 194 - 230 °F | Preferred |
| Drying Temperature | 80.0 - 85.0 °C | 176 - 185 °F | |
| Dry Time | 4 hour | 4 hour | |
| Injection Pressure | 70.0 - 100 MPa | 10200 - 14500 psi |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Clamping Force | in tons, 0.7 times the projected surface area in cm2 | |
| Flammability Rating | SE | FMVSS No. 302, 355x100x1 mm |
| Heat Resistance - Ball Test | OK | at 125°C, IEC 309 |
| OK | at 165°C, IEC 309 | |
| Holding Pressure | 90 MPa | |
| Needle Test | OK | IEC 695-2-2, 1 or 2 mm |
Users viewing this material also viewed the following:
- SABIC Innovative Plastics Cycolac® MG47 ABS (Asia Pacific)
- Ravago Manufacturing Americas Hylex® P1010G10FRMA Polycarbonate, 10% Glass Filled
- TSE Industries EcoWIND® 100 Polyurethane Resin Filament Winding (discontinued **)
- LATI Latamid 6 H2 G/20-V0 PA 6, 20% Glass Fiber Reinforced, Heat Stabilized, Flame Retardant
- Saint-Gobain Chemfab® TCN® 2000 High-Strength Leno Weave Nomex/Fiberglass Belting Material
- Eastman Tritan FX100 Copolyester
- Arlon 37N Polyimide Low-Flow
- Performance Polymers IPS II PPL-C1050 PEKK (Polyetherketoneketone) Linear Extrusion Grade
- Abatron AboCast 10-5/AboCure 50-3 Epoxy
Copyright © lookpolymers.com All Rights Reserved