Barlog Plastics KEBAFORM C 8027 POM Copolymer, 30% mineral reinforced
| Category | Polymer , Thermoplastic , Acetal (POM) , Acetal Copolymer, Mineral Filled |
| Manufacturer | Barlog Plastics |
| Trade Name | KEBAFORM |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Barlog Plastics KEBAFORM C 8027 POM Copolymer, 30% mineral reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
POM-MD30Information provided by BARLOG plastics GmbH.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.58 g/cc | 0.0571 lb/in³ | ISO 1183 |
| Linear Mold Shrinkage, Flow | 0.012 cm/cm | 0.012 in/in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm | 0.015 in/in | ISO 294-4 |
| Melt Flow | 22 g/10 min @Load 2.16 kg, Temperature 190 °C |
22 g/10 min @Load 4.76 lb, Temperature 374 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527-1 |
| Elongation at Break | 11 % | 11 % | ISO 527-1 |
| Tensile Modulus | 4.70 GPa | 682 ksi | ISO 527-1 |
| Charpy Impact, Notched | 0.500 J/cm² | 2.38 ft-lb/in² | ISO 179-1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 166 °C | 331 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 145 °C | 293 °F | ISO 75-1/-2 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Resin Type | POM-MD30 |
Users viewing this material also viewed the following:
- RheTech Products T10P250-01 10% Talc Reinforced Polypropylene Copolymer, General Purpose Black
- Network Polymers SAN 280 Water Clear
- PEAK Werkstoff DISPAL S250 Aluminum Alloy, AlSi20Fe5Ni2, Condition F
- PolyOne Geon™ Vinyl Flexible C90UB Polyvinyl Chloride, Flexible (PVC, Flexible)
- H.C. Starck Amperit® 140.2 Tungsten (W)
- Solvay TECHNYL® C 206 PA6, DRY
- Shinkong Synthetic Fibers Shinite® N602 Nylon 66
- Chase Plastics CP Pryme® NN133GL (COND, 50% RH) Nylon 66, 33% Glass Fiber Reinforced, Internally Lubricated
- Trelleborg Emerson & Cuming Eccobond® 43 Heat Cure Catalyst
Copyright © lookpolymers.com All Rights Reserved