- Nilit FRIANYL C73 GV30 Nylon 6.6/6 for injection molding, 30% glass fiber reinforced
Nilit FRIANYL C73 GV30 Nylon 6.6/6 for injection molding, 30% glass fiber reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6/66 , Nylon 66/6, 30% Glass Fiber Reinforced |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL C73 GV30 Nylon 6.6/6 for injection molding, 30% glass fiber reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6.6/6 for injection molding, medium viscosity.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | ISO 1183 |
| Water Absorption | 1.0 - 2.0 % | 1.0 - 2.0 % | ISO 62 |
| Water Absorption at Saturation | 4.5 - 5.5 % | 4.5 - 5.5 % | ISO 62 |
| Viscosity Measurement | 155 | 155 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0040 - 0.012 cm/cm | 0.0040 - 0.012 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 170 MPa | 24700 psi | ISO 2039-1 |
| Tensile Strength at Break | 180 MPa | 26100 psi | ISO 527 |
| Elongation at Break | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 9.00 GPa | 1310 ksi | ISO 527 |
| Flexural Strength | 240 MPa | 34800 psi | ISO 178 |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | DIN 53453 |
| 4.50 J/cm² @Temperature -40.0 °C |
21.4 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.900 J/cm² | 4.28 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 242 °C | 468 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 115 °C | 239 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 225 °C | 437 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Oxford Polymers C-Acetal 25GF 25% Glass Fiber Reinforced Copolymer Acetal
- P & P Technology Nickel Graphite Loaded EPDM
- Shandong Rike Chemical HELIâ„¢ HA-100 PVC Processing Aid Series (PA)
- Samsung Cheil Industries Infino® UF-1017 PC, Unreinforced FR
- Techmer ES HiFill FR® PET GF30 FR X 30% Glass Filled
- A. Schulman PP 3489-01 Polypropylene Homopolymer
- A. Schulman POLYBATCH™ Yellow 2214E Concentrate Based In Polyethylene
- EMS-Grivory Grivory® ELX 50 HNZ TPA
- ExxonMobil LDPE LD 317.09 Low Density Polyethylene Resin
- Chicago Extruded Metals BioBrass® UNS C95510 As-Cast Aluminum Bronze
Copyright © lookpolymers.com All Rights Reserved