Nilit FRIANYL B63 S Nylon 6 for injection molding
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 , Nylon 6, Unreinforced |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 S Nylon 6 for injection molding.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding, light impact modified.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 |
| Water Absorption | 2.2 - 3.2 % | 2.2 - 3.2 % | ISO 62 |
| Water Absorption at Saturation | 8.0 - 9.0 % | 8.0 - 9.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.015 - 0.025 cm/cm | 0.015 - 0.025 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 125 MPa | 18100 psi | ISO 2039-1 |
| Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 |
| Elongation at Break | 25 % | 25 % | ISO 527 |
| Tensile Modulus | 2.80 GPa | 406 ksi | ISO 527 |
| Flexural Strength | 80.0 MPa | 11600 psi | ISO 178 |
| Flexural Modulus | 2.70 GPa | 392 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU |
| NB | NB | DIN 53453 | |
| NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU | |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| 0.800 J/cm² | 3.81 ft-lb/in² | DIN 53453 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 80.0 °C | 176 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | CTI 100; IEC 112 |
| 600 V | 600 V | CTI-M 100; IEC 112 |
Users viewing this material also viewed the following:
- Polymax® Maxelast® P3850 TPE, PP Overmold or Standalone use
- Ineos Nova Zyntar® F7120 Developmental Flame Retardant Polystyrene (discontinued **)
- Special Metals INCONEL® 718SPF™ Nickel Superalloy, Annealed + Aged
- Teknor Apex Monprene® MP-2111 L2 Thermoplastic Elastomer
- SABIC Innovative Plastics LNP Thermocomp RB003 PA 66 (Europe-Africa-Middle East)
- Tra-Con Tra-Bond FDA26 Food and Drug Application Epoxy Adhesive
- TSE Industries Millathane® HT High Temperature-Resistant Millable Polyester Polyurethane with 20 PHR N220 (ISAF) Filler
- Dow Corning HV 1520/40
- DuPont Teijin Films Teijin® Tetoron® SL Polyester Film, 300 Gauge
- 3M FV037 Indoor UL Recognized White Vinyl Label Products
Copyright © lookpolymers.com All Rights Reserved