Nilit FRIANYL B63 KV40 Nylon 6 for injection molding, 40% glass ball reinforced
| Category | Polymer , Thermoplastic , Nylon , Nylon 6 |
| Manufacturer | Nilit (formerly Frisetta Polymer) |
| Trade Name | FRIANYL |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Nilit FRIANYL B63 KV40 Nylon 6 for injection molding, 40% glass ball reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Nylon 6 for injection molding.Information provided by Frisetta Polymer, which merged into Nilit Plastics
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.42 g/cc | 0.0513 lb/in³ | ISO 1183 |
| Water Absorption | 1.3 - 2.3 % | 1.3 - 2.3 % | ISO 62 |
| Water Absorption at Saturation | 5.0 - 7.0 % | 5.0 - 7.0 % | ISO 62 |
| Viscosity Measurement | 145 | 145 | Viscosity index; ISO 307 |
| Linear Mold Shrinkage | 0.0080 - 0.016 cm/cm | 0.0080 - 0.016 in/in | FRISETTA Test Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Ball Indentation Hardness | 175 MPa | 25400 psi | ISO 2039-1 |
| Tensile Strength at Break | 85.0 MPa | 12300 psi | ISO 527 |
| Elongation at Break | 12 % | 12 % | ISO 527 |
| Tensile Modulus | 4.50 GPa | 653 ksi | ISO 527 |
| Flexural Strength | 120 MPa | 17400 psi | ISO 178 |
| Flexural Modulus | 3.90 GPa | 566 ksi | ISO 178 |
| Charpy Impact Unnotched | NB | NB | DIN 53453 |
| 3.50 J/cm² @Temperature -40.0 °C |
16.7 ft-lb/in² @Temperature -40.0 °F |
DIN 53453 | |
| Charpy Impact, Notched | 0.700 J/cm² | 3.33 ft-lb/in² | DIN 53453 |
| 0.800 J/cm² | 3.81 ft-lb/in² | ISO 179/1eA |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 221 °C | 430 °F | ISO 3146 DSC |
| Maximum Service Temperature, Air | 115 °C | 239 °F | Continuous; FRISETTA Test Method |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 93 |
| Dissipation Factor | 0.020 @Frequency 1e+6 Hz |
0.020 @Frequency 1e+6 Hz |
IEC 250 |
| Comparative Tracking Index | 550 V | 550 V | CTI 100; IEC 112 |
Users viewing this material also viewed the following:
- Lubrizol Advanced Materials Pearlstick® 45-90/12 Polycaprolactone based TPU
- Momentive Performance Materials RTV160 Electronic Grade Silicone Adhesive Sealant, White
- Addiplast Addilene H 490 M10S Flame Retardant Polypropylene
- Arlon R38095R011 0.011" (0.279 mm) Partially Cross Linked Silicone Rubber with Fiberglass Substrate
- Fainplast Compounds KL 96 Flexible PVC, Insulation for High Temperatures Lead Free
Copyright © lookpolymers.com All Rights Reserved