PTS Tristar® PC-30GFR 30% Glass Reinforced Polycarbonate
| Category | Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, 30% Glass Filled |
| Manufacturer | Polymer Technology & Services, LLC (PTS) |
| Trade Name | Tristar® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | PTS Tristar® PC-30GFR 30% Glass Reinforced Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Polymer Technology and Services, LLC (PTS).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in³ | ASTM D792 |
| Water Absorption | 0.12 % | 0.12 % | 24 hrs; ASTM D570 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 128 MPa @Thickness 3.17 mm |
18500 psi @Thickness 0.125 in |
ASTM D638 |
| Elongation at Break | 3.0 % @Thickness 3.17 mm |
3.0 % @Thickness 0.125 in |
ASTM D638 |
| Flexural Strength | 155 MPa @Thickness 3.17 mm |
22500 psi @Thickness 0.125 in |
ASTM D790 |
| Flexural Modulus | 7.58 GPa @Thickness 3.17 mm |
1100 ksi @Thickness 0.125 in |
ASTM D790 |
| Izod Impact, Notched | 1.07 J/cm @Thickness 3.17 mm |
2.00 ft-lb/in @Thickness 0.125 in |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 143 °C | 290 °F | ASTM D648 |
| UL RTI, Electrical | 80.0 °C | 176 °F | |
| UL RTI, Mechanical with Impact | 80.0 °C | 176 °F | |
| UL RTI, Mechanical without Impact | 80.0 °C | 176 °F | |
| Flammability, UL94 | V-0 @Thickness 3.00 mm |
V-0 @Thickness 0.118 in |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Arc Resistance | 60 - 120 sec | 60 - 120 sec | PLC 6 |
| Comparative Tracking Index | 100 - 175 V | 100 - 175 V | PLC 4 |
| Hot Wire Ignition, HWI | 60 - 120 sec | 60 - 120 sec | PLC 1 |
| High Amp Arc Ignition, HAI | >= 120 arcs | >= 120 arcs | PLC 0 |
Users viewing this material also viewed the following:
- Nye Lubricants 132G (SO) Synthetic Oil
- Lavergne VYPET VNT 645 PET 45% Glass Reinforced
- SABIC Innovative Plastics Valox® 312 PBT (Asia Pacific)
- Solvay GEROPON® TK 32 Surfactant
- Teknor Apex Monprene® MP-1846-L3 Thermoplastic Elastomer
- Teknor Apex Sinpolene MBB1732 Low Density Polyethylene
- Teknor Apex TEKRON® 4300-D88F Thermoplastic Elastomer
- CTC X-PRO CTC PP1035 Polypropylene Homopolymer
- Hippe PF CC 203 Woven Cotton Cloth Reinforced Phenolic Resin - Sheet
- Arlon 32400R040 0.040" (1.02 mm) Uncured Silicone Rubber on PET Carrier
Copyright © lookpolymers.com All Rights Reserved